- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 126 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 126 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 144 PC
UL rated HB. 200 series recommended when V-2 rating required. 10.5 MFR. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer be supported with bioco..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 945AU PC (Asia Pacific)
Lexan* 945AU Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has a V0 UL rating and is UV stabilized, providing additiona..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | ASTM D648 |
|
Ravago Manufacturing Americas Hylex® P1332L Polycarbonate, UV Stabilized, Unreinforced
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ente..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 6.40 mm |
259
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HF1140R PC
High flow grade. Heat stabilized. Enhanced level of mold release. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade will no longer be supported with biocompatib..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HP1REU PC (Europe-Africa-Middle East)
High flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO sterilizable. Contains mold release.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HPS4 PC (Asia Pacific)
Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI).EtO, steam, e-beam, and gamma sterilizable...
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® OQ3820 PC (Asia Pacific)
High Viscosity, UV-stabilized grade for ophthalmic lenses.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® R9453 PC (Asia Pacific)
Lexan* R9453 Polycarbonate (PC) is a non-filled, non-chlorine and non-brominate flame retardant resin for general purpose, which contains 30% post-consumer recycled PC. This resin is of UL-94 V0 rat..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Colorcomp D10009 PC
LNP* Colorcomp* D10009 is a compound based on Polycarbonate resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.This data was supplied ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB SCANTEC PC S90R Polycarbonate
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 925AU PC (Asia Pacific)
Lexan* 925AU Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is UV stabilized, providing addit..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 925U PC (Asia Pacific)
Lexan* 925U Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is UV stabilized, providing additio..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 955 PC
Lexan* 955 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is available in various opaque color..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® EXL8414 PC Copolymer (Asia Pacific)
Lexan* EXL8414 is a PC/siloxane copolymer resin with medium flow, excellent low temperature impact and 25% post consumer recycle content. Limited availability and restricted color only. Higher color..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HF1110R PC (Asia Pacific)
High flow grade. Easy mold release version of LEXAN HF1110. For thin wall lighting lenses, data storage components and safety eyewear lenses.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 6.40 mm |
259
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HF1130 PC (Asia Pacific)
UV-stabilized. Good clarity, heat resistance, property retention and dimensional stability.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 4.00 mm |
259
°F @Thickness 0.157 in |
Unannealed; ASTM D648 |
|
LG Chemical Lupoy NF1005F 03R Polycarbonate Resin
Description: LUPOY NF 1005F03R, eco-friendly UL94 V0/1.5 mm, is designed for extrusion products. It combines an excellent physical property balance of heat resistance, transparency and impact streng..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRILOY D2000 PC (Asia Pacific)
LNP LUBRILOY* D2000 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-KON DD0009XP PC
LNP* STAT-KON* D-FR is a compound based on Polycarbonate resin containing Carbon. Added features of this grade include: Flame Retardant, Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-KON DD000P PC
LNP* STAT-KON* DD000P is a compound based on Polycarbonate resin containing Carbon. Added features of this material include: Electrically Conductive, Exceptional Processing.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Annealed; ISO 75-2/A |
|
Styron CALIBREâ„¢ 201-22 Polycarbonate Resin
Overview: CALIBREâ„¢ 201-22 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistanc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Annealed; ASTM D648; ISO 75-2/A |
|
Styron CALIBREâ„¢ 2061-22 Polycarbonate Resin
Overview: CALIBREâ„¢ 2061-22 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-22 provides exceptional clarity, heat resistance, impa..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Thermocomp ZWM2411 PPE+PS (Asia Pacific)
Modified PPO*, 30% mineral filled product, V-1@1.5mm, HDT 125degC, low warpage product, BK color onlyThis data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
Unannealed; ASTM D648 |
|
Teknor Apex Sinpolene GPP1610 Polypropylene
Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 10% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 258 °F | Unannealed; ASTM D648 |
|
Chase Plastics CP Pryme® AH300 Acetal Homopolymer, Recycled Content
Features: General purposeHigh heat resistanceGood chemical resistanceGood dimensional stabilityFatigue resistantLow frictionGrease resistantLow moisture absorptionOil resistantHigh rigiditySolvent r..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | |
|
Covestro Makrolon® 6385 Polycarbonate, Injection Grade
Low viscosity, flame retardant injection molding grade with easy mold release, not available in transparent colors.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was sep..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | ISO 75-1/-2 |
|
Covestro Makrolon® LTG2623 Polycarbonate
PreprocessingMax. Water content
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 258 °F | ASTM D648 |
|
RheTech Products GC20P255-712UV 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, B231 Earth Grey
Applications: Consumer goodsMiscellaneous bracketsExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 945 PC (Asia Pacific)
Lexan* 945 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is available in various opaque color..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
126
°C @Thickness 3.20 mm |
259
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP DL0039EF PC
LNP* Lubricomp* DL-0039EF is a compound based on Polycarbonate resin containing 15% PTFE. Characteristics of this grade include: Flame Retardant and Internally Lubricated.
|
|||