- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 129 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 129 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 6.40 mm |
264
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 124 PC (Asia Pacific)
17.5 MFR, for small, intricate parts. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade is no longer supported with biocompatibility information and should not ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | ASTM D648 |
|
Polymer Resources PC-FR2A-D-[color]-3 Polycarbonate, Flame Retardant, Medium Flow, UV-stabilized
Polycarbonate, Flame Retardant, Medium Flow, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | ASTM D648 |
|
Polymer Resources PC-GP2-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Medium Flow with Mold Release
Polycarbonate, FDA-compliant Feedstocks, Medium Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sa..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Unannealed; ASTM D648 |
|
Ravago Manufacturing Americas Hylon® N1213HL BK Nylon 6/6
Available in North America Filler: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedRoHS CompliantForm: Pellets Proces..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® HFD4413 PC (Asia Pacific)
Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 3.20 mm |
264
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HPS7 PC (Europe-Africa-Middle East)
Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma sterilizable. ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 3.20 mm |
264
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® LUX1619 PC
Lexan* LUX1619 Polycarbonate resin is an extrusion grade. It is UL94 HB rated. It was designed for high light reflectance.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 3.20 mm |
264
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® LUX2619 PC (Europe-Africa-Middle East)
Lexan* LUX2619 Polycarbonate resin is an extrusion grade. It is UL94 V-2 rated at 1.5 mm. It was designed for high light reflectance.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 3.20 mm |
264
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® OQ3820 PC
High Viscosity, UV-stabilized grade for ophthalmic lenses.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP DL001 PC
LNP* LUBRICOMP* DL001 is a compound based on Polycarbonate resin containing 5% PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | ASTM D648 |
|
Nylene® Naxel™ PC35CV Polycarbonate
Description: Naxel™ PC35CV is a 12 melt, virgin, general purpose polycarbonate. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | ASTM D648 |
|
Polymer Resources PC-FR3A-D-[color]-3 Polycarbonate, Flame Retardant, High Flow, UV-stabilized
Polycarbonate, Flame Retardant, High Flow, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informat..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 6.40 mm |
264
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HP2 PC (Asia Pacific)
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains m..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC
LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing 20% Milled Glass, 15% PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 3.20 mm |
264
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC
LNP* Lubricomp* Lexan_LF1530A compound is a 30% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | unannealed, .125in; ASTM D648 |
|
Star Plastics PC741 Molding Grade PC
Information provided by Star Plastics, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 3.20 mm |
264
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP DX09402 PC
LNP* THERMOCOMP* DX09402 is a compound based on Polycarbonate containing Proprietary Filler(s).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 6.40 mm |
264
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Infino® EN-1052 PC, FR
Non-halogen flame-retardant material with high heat resistance that can be used in battery chargerInformation provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | ISO 75 |
|
Teijin Panlite® LN-1250G Flame Resistant, Translucent Polycarbonate Resin
Flame retardant and mold release grade with normal fluidity, which is suitable for injection molding applications.Applications:Electric, electronic and business machine components that need flame re..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS
LNP* Thermodcomp* Noryl_PCN2910 compound is a 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Unannealed; ASTM Data |
|
Styron CALIBREâ„¢ 200 6 Polycarbonate, General Purpose
CALIBRE® 200 series are general purpose, UL listed Polycarbonate resins formulated to comply with the applicable FDA and European regulations governing food contact(1). CALIBRE 200 series resins ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
129
°C @Thickness 6.40 mm |
264
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Noryl PKN4736 PPE+PS (Asia Pacific)
PPE+PS. FDA compliant. High heat. Excellent ESCR. Extrusion. Microwavable. Food packaging uses.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | ISO 75 |
|
Teijin Panlite® LV-2250Z Transparent and Weather Resistant grade Polycarbonate Resin
Typical injection molding grade that has weather resistance and is bluish-tinted to exhibit clear color.Applications:Components of electric, electronic, business machine and industrial equipment com..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Asia Pacific)
PPE+PS blend. 10% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including wate..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | |
|
Covestro Makrolon® 2607 Polycarbonate, Injection Grade
Easy flowing injection molding grade with easy mold release and UV stabilizer.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially a..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | |
|
Covestro Makrolon® 2807 Polycarbonate, Injection Grade
Medium flowing injection molding grade with easy mold release and UV stabilizer.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | |
|
Aclo Accutech Polypropylene Copolymer CP0436G25M5CL Glass/Mineral Reinforced Coupled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | ASTM D648 |
|
Polymer Resources PPX/NY GP2 Modified PPO, Medium Heat PPX/Nylon 6,6 Alloy
(Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
|
|||