- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 133 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 133 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Annealed 120°C, 2hrs; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® LUX7189 PC (Europe-Africa-Middle East)
Lexan* LUX7189 is an injection moldable, high light reflectance FR grade. Contains non-brominated, non-chlorinated flame retardant systems.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® SLX2231D PC Copolymer
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Diffusion colors.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® SLX2231T PC Copolymer
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Americas regio..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® SLX2231T PC Copolymer (Asia Pacific)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 6.35 mm
|
271
°F <br>@Thickness 0.250 in
|
Unannealed; ASTM D648 |
|
PolyOne Stat-Tech™ PC-08CF/000 FR V0 Polycarbonate (PC)
Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® SLX2231T PC Copolymer (Europe-Africa-Middle East)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Europe-Africa-..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® SLX2271T PC Copolymer (Europe-Africa-Middle East)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL36P PC
LNP* Lubricomp* DFL36P is a compound based on Polycarbonate containing 30% Glass Fiber 15% PTFE. Added features include: Exceptional Processing. Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL36P PC
LNP* Lubricomp* DFL36P is a compound based on Polycarbonate containing 30% Glass Fiber 15% PTFE. Added features include: Exceptional Processing. Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS (Asia Pacific)
PPE+PS blend. 20% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. Dielectric strength. Dimensional stability. Suitable for E/E applications.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP ZFL34 PPE+PS
LNP* LUBRICOMP* ZFL34 is a compound based on PPE+PS resin containing 20% Glass Fiber, 15% PTFE. Added feature of this gradae is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP ZFL34 PPE+PS
LNP* LUBRICOMP* ZFL34 is a compound based on PPE+PS resin containing 20% Glass Fiber, 15% PTFE. Added feature of this gradae is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Lubricomp ZFL34 PPO
LNP* Lubricomp* ZFL34 is a compound based on Modified PPO containing glass fiber and PTFE.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-KON DX04490 PC
LNP* STAT-KON* DX04490 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON DX98477 PC
LNP* STAT-KON* DX98477 is a compound based on Polycarbonate containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP MF006S PP
LNP* THERMOCOMP* MF006S is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
Samyang Trirex® 3020IR Polycarbonate with Heat Stabilizer
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020IR is a high flow grade with added heat stabilizers, separating materials and stain..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
Samyang Trirex® 3020U UV Stable Polycarbonate
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020U is a high flow, UV Stable grade.Information provided by Samyang.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP VERTON NV004E PC+ABS
LNP VERTON* NV004E is a compound based on PC+ABS Blend resin containing 20% Long Glass Fiber. Added features of this material include: Easy Molding, Structural.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP VERTON NV004E PC+ABS (Europe-Africa-Middle East)
LNP VERTON* NV004E is a compound based on PC+ABS Blend resin containing Long Glass. Added features of this material include: Easy Molding.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC
LNP THERMOCOMP* DFZ22P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 10% Milled Glass. Added features of this material include: Exceptional Processing.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP MFB82I PP (Europe-Africa-Middle East)
LNP* Thermotuf* MFB82I is a compound based on Polypropylene resin containing Glass Fiber, Glass Bead.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOTUF DF008EI PC (Asia Pacific)
LNP* Thermotuf* DF008EI is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, High Impact.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
A. Schulman ComAlloy Comtuf® 106 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled, Impact Modified, UL
Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
A. Schulman ComAlloy Lubrilon® 511 Polycarbonate, Glass Fiber/PTFE, UL
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® FXG154 PC (Europe-Africa-Middle East)
FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended.This data was supplied by SABIC-IP for the Europe-Africa-Middle East r..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® ML6230 PC Copolymer (Europe-Africa-Middle East)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. Available in transparent and tinted colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
Samyang Trirex® 3020R Polycarbonate with Heat Stabilizer
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020R is a high flow grade with added heat stabilizers and separating materials.Informa..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® SLX2231D PC Copolymer (Europe-Africa-Middle East)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Diffusion colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON ME003S PP
LNP* STAT-KON* ME003S is a compound based on Polypropylene resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Heat Stabilized.
|
|||