- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 146 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 146 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
RheTech Products F15-01 35% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Black
Applications: HousingsBattery traysInjection molding conditions reported in table.Information provided by RheTech Products.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
Oxford Polymers 30GF 30% Glass Fiber Filled Polycarbonate for Injection Molding
30% Glass Fiber Filled Polycarbonate for Injection MoldingInformation provided by Oxford Polymers.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
Oxford Polymers 40GF 40% Glass Fiber Filled Polycarbonate for Injection Molding
40% Glass Fiber Filled Polycarbonate for Injection MoldingInformation provided by Oxford Polymers.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
146
°C @Thickness 6.40 mm |
295
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 3413R PC
30% GR, provides improved mechanical properties and UL94V-1 rated at 0.058"". Internal mold release added.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
146
°C @Thickness 6.40 mm |
295
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 3413R PC (Asia Pacific)
Lexan* resin 3413R is a flame retardant polycarbonate grade with 30% glass fiber reinforcement to meet UL 94 V1 listing at 1.5mm. This grade can be considered for applications requiring higher stiff..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
Polymer Resources PC-G30 Polycarbonate, 30% Glass Reinforced
Polycarbonate, 30% Glass ReinforcedFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
Polymer Resources PC-G40 Polycarbonate, 40% Glass Reinforced
Polycarbonate, 40% Glass ReinforcedFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
146
°C @Thickness 3.18 mm |
295
°F @Thickness 0.125 in |
Annealed; ASTM D648 |
|
PolyOne Maxxam™ FR QD 818.Y001 Polypropylene, Unspecified (PP, Unspecified)
Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | |
|
Lehmann & Voss LUVOCOM® 50-7586 Polycarbonate, with carbon fiber
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts with low warpage and..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | Unannealed (0.250"); ASTM D648 |
|
LTL Color Compounds ColorFast® PCGF130 Polycarbonate, 30% Glass-Filled
30% glass-filled grade polycarbonateAll information provided by LTL Color Compounders, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP LX00430 PEEK
LNP* LUBRICOMP* LX00430 is a compound based on Pelyetheretherketone containing Proprietary Fillers. Added feature of this grade is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-KON DX05474 PC (Asia Pacific)
LNP* Stat-kon* DX05474 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Ret..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6 GF5 L 5% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 5% Filler by WeightAdditive: Lubricant Features: LubricatedAppearance: Natural ColorInformation provided by ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
146
°C @Thickness 3.20 mm |
295
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC (Asia Pacific)
LNP* THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Low Extractible.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
146
°C @Thickness 6.40 mm |
295
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Europe-Africa-Middle East)
LNP* Thermocomp* Lexan_LGK3020 compound is a glass reinforced, flame retardant material.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
146
°C @Thickness 3.20 mm |
295
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL PPX PPX640 PPE+PP
40% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
146
°C @Thickness 3.20 mm |
295
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Lubricomp LL003E PEEK
LNP* Lubricomp* LL003E is a compound based on Polyetheretherketone (PEEK) containing PTFE. Characteristics of this grade are: Easy Molding and Internally Lubricated.This data was supplied by SABIC..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
Plastics Group Polifil® GFPC-20 20% Glass-Reinforced Polycarbonate
Polifil® GFPC series compounds offer a combination of improved dimensional stability and decreased flammability. The excellent balance of physical properties make the Polifil® glass-filled polycar..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
Asahi Kasei Thermylene® P6-20FG-1812 20% Glass Fiber Reinforced, UV Stabilized
Information provided by Asahi Thermofil
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
Asahi Kasei Thermylene® P6-20FG-2153 20% Glass Fiber Reinforced, Heat Stabilized
Information provided by Asahi Thermofil
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
Ashley Polymers Ashlene® P1440 Polycarbonate, 40% Glass Reinforced
A 40% glass reinforced polycarbonate for maximum mechanical strength and thermal properties. P1443 with UV stabilizer.Data provided by the manufacturer
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
|
Custom Resins Norpex® GF3 PPE (Polyphenylene Ether), 30% Glass Filled
(discontinued **)
Properties for dry as molded samples.Data provided by the manufacturer
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 294 °F | ASTM D648 |
|
RheTech Products GC43P250-01 43% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Black
Applications: Consumer goodsFunctional supportsHead lamp bracketsDurable GoodsInjection molding conditions reported in table.Information provided by RheTech Products.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
146
°C @Thickness 6.40 mm |
295
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Asia Pacific)
Glass reinforced. Flame retardant.
|
|||