- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 150 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 150 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
150
°C @Thickness 3.20 mm |
302
°F @Thickness 0.126 in |
Unannealed; ASTM D648 |
|
Ovation Polymers OpteSTAT™ NC PK 8010 Polyetheretherketone based Carbon Nanotube Compound
Material resistivity can be tailored to the application, while retaining the physical and thermal properties of the base polymer. Applications include components of disk drives, business machines or..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Unannealed; ISO 75-2/C |
|
Pasargad Polymer Peyvand Pasalen 3P-H3130B Polypropylene, 30% Glass Fiber Reinforced
Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Automotive Exterior PartsAutomotive Interior PartsInformation provided by Pasargad Poly..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® FXM4701 PPC (Asia Pacific)
LEXAN FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.This data was supplied by SABIC-IP for the Asia Paci..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
Asahi Kasei Tenac® GT525 Acetal Homopolymer, 25% Glass Beads
(discontinued **)
25% glass beads-filled grade with superior isotropic dimensional stability.Applications: Speedometer frames.This product is not a part of the standard product line dated 2003.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
150
°C @Thickness 3.17 mm |
302
°F @Thickness 0.125 in |
ASTM D648 |
|
Covestro Apec® DP9-9343 High-Heat Polycarbonate, UV Stabilized
(discontinued **)
Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 - 250 °C | 302 - 482 °F | Average value: 180 °C Grade Count:32 |
|
Overview of materials for Phenolic, Novolac, Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral Filled". Each property range of values reported is minimum and maximum values..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | |
|
Lehmann & Voss LUVOCOM® 50-7078/GY Polycarbonate, with carbon fiber and PTFE
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Electrically conductive, suitable for cont..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | |
|
Lehmann & Voss LUVOCOM® 50-8025 Polycarbonate, with glass fiber and PTFE
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75 |
|
GEHR Plastics PA 6.6-30GF Nylon 6.6, 30% Glass Fiber, Dry
Polyamide shows both a high thermostability and high stiffness, hardness and toughness. These are some of the main characteristics. Due to the fact, that the good mechanical characteristics will be ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
LG Chemical LUPOL LW-4407 Low Warpage Polypropylene, 40% Glass Fiber/Mineral Filler Reinforced, Heat Resistant
LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | |
|
LATI Laticonther 82 CP1/800 PA12
High thermal conductivity product based on Polyamide 12 (PA12). Special fillerAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indus..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | 80*10*4mm, Cut; ISO 75-1&2 |
|
SABIC Innovative Plastics SABIC PPCOMPOUND G3220A PP
SABIC® PPcompound G3220A is a general purpose, 20% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS is 209767996.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Ultem HATX100 PEI+PCE (Asia Pacific)
Higher impact, high flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Valox® 815F PBT+PET (Europe-Africa-Middle East)
PBT+PET, 15% Glass, Mold Release, Heat Stabilized, For food contact applications
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
150
°C @Thickness 6.40 mm |
302
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Infino® VB-3100G PBT/ABS, Glass Filled FR
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
150
°C @Thickness 3.20 mm |
302
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP VERTON MV00ES PP
LNP* VERTON* MV00ES is primarily a concentrate used for blending purposes. This is a 70% long glass fiber Polypropylene compound. Added features of this grade are: Heat Stabilized
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
150
°C @Thickness 6.40 mm |
302
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL N300 PPE (Asia Pacific)
High Heat 150deg.C, FR V-0
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FXP 6630 Nylon 6.6 Polypropylene Alloy
DescriptionPolyfort® FXP 6630 is a nylon 6.6 / polypropylene alloy with 30% wollastonite.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
Unitika AXF-1500-05 Dry
Characteristics: Lubricant grade of AX1500, excellent in heat and chemical resistancesInformation provided by Unitika Ltd.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene
DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene
DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM-D648 |
|
Polyram Polytron P35B03 Copolymer Polypropylene, Chemically Coupled 35% Long Glass Fiber
A CHEMICALLY COUPLED 35% LONG GLASS FIBERS REINFORCED BLACK POLYPROPYLENE, HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | |
|
Covestro Apec® HT KU 1-9340 High-Heat Polycarbonate
Transparent and opaque shades possible.Applications: Medical sector: superheated steam sterilization.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Ba..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | |
|
Covestro Apec® HT KU 1-9341 High-Heat Polycarbonate
Transparent and opaque shades possible.Applications: Lighting, automotive and household goods, light covers, indicator and brake light lenses.Information provided by Bayer.As of 1 September 2015, Ba..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® LV-2H PA12-GF20
Product description: Grilamid LV-2H is a 20% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following product profile: very low water absorptionhigh dimensiona..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
|
Eurostar Starpylen MX06050 PP, 30% Glass Filled, Injection Molded
Starpylen MX06050 is a 30% Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75 |
|
BASF Ultramid® B3GK24 10/20% Glass Bead/Fiber Filled PA6 (Dry)
Ultramid B3GK24 is 30% combined glass-fiber and glass bead injection molding PA6 grade for industrial articles having very high dimensional stability.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | 0.5 inch; ASTM D648 |
|
PlastxWorld CEVIAN® A2604 20% GF PA/ABS Alloy, Conditioned
Property data is for samples at equilibrium moisture (1.1%)These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWo..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | 80*10*4mm, Cut; ISO 75-1&2 |
|
SABIC Innovative Plastics SABIC PPCOMPOUND G3230A PP
SABIC® PPcompound G3230A is a general purpose, 30% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS ID is 109612410
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 - 170 °C | 302 - 338 °F | ISO 75 Af |
|
Vyncolit 3520 CG Novolac Phenolic
Graphite filled phenolic molding compound with excellent dimensional stability. Self-lubricating and has a low coefficient of friction. Not suitable for electrical applications.USES: Gas meter par..
|
|||