- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 190 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 190 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | ASTM D648 |
|
Oxford Polymers 20GF 20% Glass Fiber Reinforced ABS, Flame Retardant
20% Glass Fiber Reinforced ABS, Flame RetardantInformation provided by Oxford Polymers.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
88.0
°C @Thickness 3.20 mm |
190
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Cycoloy® CE3210 PC+ABS (Europe-Africa-Middle East)
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics GELOY HRA222F ASA+PC (Europe-Africa-Middle East)
Geloy HRA222F is a multi-purpose, chlorine and bromine free flame retardant ASA-PC alloy for injection moulding processes. This grade has a F1 rating according UL746C. Typical properties as measured..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | Unannealed (0.250 in); ASTM D648 |
|
Ravago Manufacturing Americas Hylac® HF224 ABS
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Rava..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
|
PTS Trilac® TR558-CL ABS- Transparent ABS
Information provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | Annealed (2 hours @ 176°F); ASTM-D648 |
|
Ineos ABS Lustran® Guardian™ 732 ABS, Extrusion Grade
Lustran® Guardian™ ABS 732 is an extrusion grade resin designed for use in thermoformed refrigerator and freezer liner applications. It is suitable for use with 245fa PU foams.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | |
|
Ineos Styrenics Avantra® 597N Polystyrene (NAFTA)
High-impact grade of polystyrene with improved impact strength and heat resistance, developed for injection molding and extrusion/thermoforming applications.Information provided by BASF.Ineos Styren..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ISO 75A |
|
Lucite International Diakon® LG156 Acrylic Bead Polymer, High Transparency
PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648-95 |
|
Multibase Multi-ABS 3832 Natural
Multi-ABS 3832 is specially formulated for ease of processability, controllability, and thin-walled parts where higher than normal temperatures are being used. This product also shows higher than n..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Annealed; ASTM D648 |
|
Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF)
Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion.Features: High Viscosity; HomopolymerAdditional Properties: Crystallization Heat - ASTM D3418 46.0 ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
88.0
°C @Thickness 3.20 mm |
190
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON FX98501 PE
LNP* STAT-KON* FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
|
Shuman 811 Black Polystyrene Medium Impact
Injection molding and extrusion grades, easy processability, good gloss, good surface appearance.Data provided by the manufacturer.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
88.0
°C @Thickness 6.40 mm |
190
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® NH-0927 ABS, Unreinforced FR
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
88.0
°C @Thickness 6.40 mm |
190
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® WR-9310 ASA, Unreinforced Heat Resistant
Heat resistant ASA that is used in the interior/exterior material of automobileInformation provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® LDPE 0098 S LE
Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforAdditive: Heat StabilizerFeatures: Low ExtractablesInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
DescriptionPolyfort® FPP 1200H is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene
DescriptionPolyfort® FPP 1285H is a 20% glass reinforced copolymer polypropylene compound. It has good impact and heat resistance. Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene
DescriptionPolyfort® FPP 1285H is a 20% glass reinforced copolymer polypropylene compound. It has good impact and heat resistance. Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | unannealed; ISO 75 |
|
Chi Mei Polylac® PA-716 ABS - High Flow
High flow, medium impact
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | 0.125";; ASTM D648 |
|
Diamond Polymers DIAMALOY GLY 7510 High Heat ASA Weatherable Polymer
Diamaloy GLY 7510 resin is a high gloss, high heat and high impact grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. This product is rated f1 by UL and be customed..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | unannealed; ISO 75 |
|
Chi Mei Polylac® PA-757 ABS
High gloss, medium impact
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Method A - Annealed; ASTM D-648 |
|
Bhansali Engineering Abstron AN-450 EVM Flame Retardant ABS Grade
Information provided by Bhansali
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | |
|
Aclo Accucomp ABS ABS892EL High Heat Grade |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
|
Chem Polymer Chemlon 100 Nylon 66, Lubricated GP
A medium viscosity, general purpose injection molding grade nylon 66. Internally lubricated for excellent feed and mold release properties.Data provided by the manufacturer, Chem Polymer.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
88.0
°C @Thickness 3.20 mm |
190
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CY6310 PC+ABS (Asia Pacific)
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or la..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics GELOY CR7500 ASA
High heat ASA with optimum flow-impact balance. For Automotive applications and Automotive colors only.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
88.0
°C @Thickness 3.20 mm |
190
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Xenoy® X6320 PBT+PC
X6320 is a mineral filled PBT/PC resin developed for automotive painted doorhandles. Key advantages are excellent surface finish, easy processing and paint quality.This data was supplied by SABIC-IP..
|
|||