- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 196 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 196 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C | 196 °F | ASTM D-648 |
|
Plaskolite West Optix® CP - 61 General Purpose Acrylic Resin
Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Cycoloy® C3650 PC+ABS
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Cycoloy® C3650 PC+ABS (Europe-Africa-Middle East)
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 - 163 °C | 196 - 325 °F | Average value: 149 °C Grade Count:35 |
|
Overview of materials for Acetal Copolymer, 20% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% ar..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
91.1
°C @Thickness 3.18 mm |
196
°F @Thickness 0.125 in |
Annealed; ASTM D648 |
|
PolyOne Edgetek® AS-20GF/000 Acrylonitrile Butadiene Styrene (ABS)
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Delrin® 327UVE NC010 Acetal Homopolymer
(Unverified Data**)
Delrin® 327UVE NC010 (formerly DE20554) is a medium-high viscosity acetal homopolymer with UV stabilizers having extremely low VOC emissions, developed for automotive interior applications.Informat..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 - 180 °C | 196 - 356 °F | Average value: 104 °C Grade Count:39 |
|
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled". Specific grades with glass content betwe..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ASTM D648 |
|
LG Chemical HI835S PMMA, Impact Resistant Grade
Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
91.0
°C @Thickness 6.40 mm |
196
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical MA210 ABS, Low Gloss
Feature: Extrusion Molding, General Purpose, Low GlossApplication: Automotive Sheet, Semi-Conductor TrayCAS No. 9003-56-9Information provided by LG Chemical
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75-1,-2 |
|
Ineos ABS Lustran® ABS 640 Injection Molding Grade
Lustran® ABS 640 has high impact strength and is injection molding grade.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75-1,-2 |
|
Ineos ABS Lustran® ABS 650 Injection Molding Grade
Lustran® ABS 650 has high impact strength, high flow, and is injection molding grade.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
91.0
°C @Thickness 3.20 mm |
196
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal
LNP LUBRILOY* KL201 is a compound based on Acetal resin containing Proprietary Lubricant. PTFE. Added feature of this material is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Xenoy® X4810 PBT+PC (Europe-Africa-Middle East)
Xenoy X4810 is a hydrostable, High Modulus Ductile PC/PBT blend. This resin provides low temperature (below 0C) ductile impact behaviour, high chemical resistance, very low creep, low CTE, excellent..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75 |
|
Styrolution Novodur® 530 ABS
Novodur 530 is an extrusion grade optimized for sheet applications. It has high impact properties, high modulus and good thermoforming.Information provided by Styrolution
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75 |
|
Teijin Multilon DN-3510F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 10 % filler. Improved stiffness and high fluidity realizes a thin wall..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
91.0
°C @Thickness 6.40 mm |
196
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® ST-0185 ABS, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
91.0
°C @Thickness 6.40 mm |
196
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® QU-0191S ABS, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | 0.5 inch; ASTM D648 |
|
PlastxWorld CEVIAN® E11 Inherently Static Dissipative ABS
These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | DIN 53461 |
|
Polyram RamShine PV801 ABS, Impact Modified
Impact modified ABS for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75-1,-2 |
|
Covestro Bayblend® FR3100 TV PC/ABS Blend
Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Injec..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C | 196 °F | 0.25 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
|
Diamond Polymers ABS 3003 MC
Description: High Heat Plating GradeInformation provided by Diamond Polymers, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C | 196 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
|
Diamond Polymers ASA S910
Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C | 196 °F | |
|
Aclo Accutech ABS ABS831G30L Glass Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ASTM D648 |
|
Ineos Nova 5100 High Impact Polystyrene
(discontinued **)
Good balance of toughness and rigidity, USP Class VIApplications: Spools and reels, Thermoformed and molded packaging, Photographic cartridges, AppliancesProperties were determined on injection mold..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ASTM D648 |
|
Ineos Nova 5104 High Impact Polystyrene
(discontinued **)
Good balance of toughness and rigidity, USP Class VIApplications: Spools and reels, Thermoformed and molded packaging, Photographic cartridges, AppliancesProperties were determined on injection mold..
|
|||