- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 197 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 197 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 386 °F | ASTM D648 |
|
Penn Fibre Pennite® 4512 Nylon 6, 12% Glass Fiber Reinforced (PA6)
PENNITE® 4512 is a 12% glass fiber reinforced, black pigmented, thermally modified, type 6 nylon, available in sheets and rolls for high performance thermoforming and fabrication applications. PENN..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 (Asia Pacific)
LNP* Lubricomp* IFL34 is a compound based on Nylon 6/12 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1010K PEI (Asia Pacific)
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1010KM PEI (Asia Pacific)
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1110R PEI
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1110R PEI (Asia Pacific)
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1110R PEI (Europe-Africa-Middle East)
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1110V PEI
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics ULTEM 2410EPR PEI
40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. ECO Conforming, UL94 V0 listing.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics ULTEM 2410EPR PEI (Asia Pacific)
40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. ECO Conforming, UL94 V0 listing.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 9011 PEI
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming. Improved processability for Fiber extrusion.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® IQ8280SF PBT+PET
Valox iQ8280SF resin is an environmentally responsible, low carbon footprint, and sustainable resin. Valox iQ8280SF resin offer Super High Flow characteristics combined with high modulus and excell..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP Stat-kon PE002 PA 6
LNP* Stat-kon* PE002 is a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP Stat-kon PE002 PA 6 (Asia Pacific)
LNP* Stat-kon* PE002 is a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia P..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Stat-kon PE002 PA 6 (Asia Pacific)
LNP* Stat-kon* PE002 is a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia P..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP IC006 PA 6/12
LNP* THERMOCOMP* IC006 is a compound based on Nylon 6/12 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP IC006 PA 6/12 (Asia Pacific)
LNP* Thermocomp* IC006 is a compound based on Nylon 6/12 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1010KM PEI
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM AUT200 PEI
Transparent high flow Polyetherimide (Tg 217C). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperat..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics ULTEM HU2410 PEI
40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® V4860HR PBT (Europe-Africa-Middle East)
30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM D648 |
|
Plenco 00732 Melamine-Phenolic, Granular, Compression Molded
PLENCO 00732 is a melamine-phenolic copolymer molding compound, exhibiting excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 007..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
|
Eurostar Star L PA6 30V D31 PA6, Glass Filled, Injection Molding
Star L PA6 30V D31 is a Molybdenum Disulfide Lubricated, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
|
Eurostar Star L PA6 30V D51 PA6, Glass Filled, Injection Molding
Star L PA6 30V D51 is a PTFE Lubricated, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM Test |
|
BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Dry)
Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM D648 |
|
A. Schulman ComAlloy Comtuf® 613 Nylon 6, Glass Reinforced, Impact Modified
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM D648 |
|
Adell BT-34 Nylon 6, 20% Glass Reinforced; Impact Modified
Data provided by Adell Plastics, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM D648 |
|
A. Schulman ComAlloy Comtuf® 615 Nylon 6, Glass Reinforced, Impact Modified
Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12
LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System.
|
|||