- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 201 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 201 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYshine PBT D231 GF30 PBT, Glass-Fiber Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Unannealed; ISO 75-2/C |
|
Pasargad Polymer Peyvand Pasadur 3P-H8130B PBT, 30% Glass Fiber Reinforced
Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Automotive Exterior PartsAutomotive Interior PartsInformation provided by Pasargad Poly..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.18 mm |
394
°F @Thickness 0.125 in |
Unannealed; ASTM D648 |
|
PolyOne Edgetek® PI-30GF/000R BLACK Polyether Imide (PEI)
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.20 mm |
394
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP PFL36 PA 6
LNP* LUBRICOMP* PFL36 is a compound based on Nylon 6 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.20 mm |
394
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP PFL36 PA 6 (Asia Pacific)
LNP* Lubricomp* PFL36 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1000F PEI
Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0, V2 and 5VA listing. US FDA and EU Food Contact Compliant, NSF 51 Listing. Effective June, 2007 this grade will no long..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1000FV PEI
Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact Compliant, NSF 51 Listing.This data wa..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1000FV PEI (Europe-Africa-Middle East)
Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact Compliant, NSF 51 Listing.This data wa..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1000R PEI (Asia Pacific)
Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0, V2 and 5VA listing.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1000RV PEI
Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1000RV PEI (Europe-Africa-Middle East)
Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Europe-Afr..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1000V PEI
Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact compliant, NSF 51 listing, compliant in ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.20 mm |
394
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 2310EPR PEI (Asia Pacific)
30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRILOY RF203AXH PA 66
LNP* LUBRILOY* RF203AXH is a compound based on Nylon 66 resin containing 15% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.20 mm |
394
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM CRS5011R PEI (Asia Pacific)
Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM HU1000 PEI
Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM HU1000E PEI (Asia Pacific)
Transparent, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.20 mm |
394
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM SF2260 PEI Blend (Asia Pacific)
High flow Ultem for thin wall application
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.20 mm |
394
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON EX11402 PEI
LNP* STAT-KON* EX11402 is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.20 mm |
394
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 (Asia Pacific)
LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.20 mm |
394
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10
LNP* THERMOCOMP* QF0069 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1000E PEI (Europe-Africa-Middle East)
Transparent, standard flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant. US FDA and EU Food Contact compliant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1000EF PEI
Transparent, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, U.S. FDA and EU Food Contact compliant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 3.20 mm |
394
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM UF5011S PEI (Europe-Africa-Middle East)
Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP PF008QS PA 6
LNP THERMOCOMP* PF008QS is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized, Reduced Moisture.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | ASTM D648 |
|
Plenco 7080 Phenolic, Nodular, Compression Molded
PLENCO 07080 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength properties along with outstanding resistance to cracking and degradation from soap and de..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | ISO 75-1, 2 |
|
Polyplastics Duranex® CN7740XB Polybutylene Terephthalate (PBT), Super low warpage, GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | 1/4''; ASTM D648 |
|
Ensinger TECAPEI® made from Ultem® 1000 PEI
TECAPEI™ is an amorphous thermoplastic polyetherimide (PEI) made from Sabic Innovative Plastics' Ultem® 1000 and 2000 series resins. The unreinforced 1000 series materials are translucent amber in..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1000E PEI
Transparent, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming. US FDA and EU Food Contact compliant, NSF 51 Listing. Effective June, 2007 this grade will no longer..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
201
°C @Thickness 6.40 mm |
394
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1000EF PEI (Europe-Africa-Middle East)
Transparent, enhanced flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS. US FDA and EU Food Contact compliant.
|
|||