- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 204 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 204 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | Unannealed; ASTM Data |
|
Dow Questra® WA202 High Heat Syndiotactic Polystyrene, 30% Glass Filled
(discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 - 212 °C | 400 - 414 °F | Average value: 209 °C Grade Count:19 |
|
Overview of materials for Polyetherimide (PEI), 30% Glass Fiber
This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 30% Glass Fiber". Specific grades with glass content between 25% and 34% are included. E..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Europe-Africa-Middle East)
LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ISO 75/Af |
|
Solvay TECHNYLSTARâ„¢ S 216 V30 PA6, 30% glass filled, DRY
Description: TECHNYL STAR TM Polyamide, reinforced with 30% of glass fiber, for injection molding. Characterized by a high fluidity of the melt.Available in: Asia Pacific, Europe and North AmericaPr..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
204
°C @Thickness 6.40 mm |
399
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM DH1004 PEI (Asia Pacific)
High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
204
°C @Thickness 6.40 mm |
399
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM DH1004 PEI (Europe-Africa-Middle East)
High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. RoHS compliant and UL94 V0 listed.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill FR® PA6 GF25 FR IM 25% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 25% Filler by WeightAdditive: Flame Retardant and Impact ModifierFeatures: Flame Retardant and Impact Modifi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6 GF18 HS L 18% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 18% Filler by Weight Additive: Lubricant and Heat StabilizerFeatures: Heat Stabilized and LubricatedInformat..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6 GF20 L UV BK 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by Weight Processing Method: Injection MoldingInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6 GF20 RM BK 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by Weight Features: Low Moisture AbsorptionAppearance: BlackInformation provided by TP Composites..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® R60 G33-L 33% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: LubricantFeatures: LubricatedAppearance: Natural ColorTPCI# 9208102Information..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP PFB55 PA 6 (Europe-Africa-Middle East)
LNP* THERMOCOMP* PFB55 is a compound based on PA 6 resin containing Glass Bead, Glass Fiber.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
|
Sumitomo Bakelite Durez® 32633 Glass Filled Phenolic, Injection Grade
Durez 32633 Black Phenolic is a two-stage, glass filled, special purpose molding compound. It is designed for applications requiring high physical strengths, dimensional stability, and heat resista..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
|
Sumitomo Bakelite Sumikon® PM-9501 Glass-Filled Phenolic, Compression Grade
Sumikon PM-9501 is a two stage glass fiber and mineral filled black phenolic special purpose molding compound. It is especially designed for applications requiring high strength and dimensional s..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
|
Sumitomo Bakelite Sumikon® PM-9501 Glass-Filled Phenolic, Injection Grade
Sumikon PM-9501 is a two stage glass fiber and mineral filled black phenolic special purpose molding compound. It is especially designed for applications requiring high strength and dimensional s..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
|
A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
|
Adell BR-34 Nylon 6, 20% Glass Reinforced
Data provided by Adell Plastics, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM Data |
|
BASF Capron® 8232G HS 25% Glass-Filled Nylon 6 (Dry)
(discontinued **)
Capron 8232G HS is a heat stabilized, 25% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. Its resista..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
|
PolyOne Edgetek® PI-20GM/000 L Polyetherimide (PEI), Glass Filled
(discontinued **)
Description/Features:Milled Glass Fiber ReinforcedHigh FlowPolyOne First ChoiceInformation provided by PolyOne Corporation.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 - 220 °C | 399 - 428 °F | Average value: 211 °C Grade Count:26 |
|
Overview of materials for Polyethersulfone (PES), 20% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 20% Glass Fiber Filled". Each property range of values reported is minimum and m..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
|
Plenco 7697 Phenolic, Granular, Compression Molded
PLENCO 07697 is a black, two stage, improved impact phenolic molding compound. It has been specifically formulated for automotive pulleys. PLENCO 07697 is the same formulation as VALITE 697-A.Inform..
|
|||