- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 207 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 207 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D648 |
|
Nylene® 4114-14 GL (HS) , 14% Glass Fiber Reinforced, Impact Modified Nylon 6/6
Description: Nylene® 4114-14 GL (HS) is a 14% glass reinforced, high impact nylon 6/6. 4114-14 GL is automotive approved. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resin..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D-648 |
|
PlastiComp Complet® LGF30 - PA6 Nylon 6, 30% Long Glass Fiber Reinforced
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 6 with 30% long glass fiber reinforcementInformation provided by PlastiComp, Inc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D648 |
|
Quantum PPSU
Information provided by Quantum Advanced Engineering Plastics
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D648 |
|
Shell Carilon® DB6G6P30 Polyketone, Lubricated, Glass-Reinforced, Injection Molding Grade
(discontinued **)&l
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DA6P2L10 is a high-performance lubricated injection molding grade with mechanical properties which ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75 |
|
GEHR Plastics PPSU Polyphenylenesulfone
Polyphenylenesulfone is an amorphous material, with improved impact and hydrolysis resistance compared to PSU. The usual operating temperature is approximately 180°C. The extremely high notched i..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 3.20 mm |
405
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP WFL33 PBT
LNP* LUBRICOMP* WFL33 is a compound based on PBT containing 15% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 6.40 mm |
405
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 2313 PEI (Asia Pacific)
30% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific regi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 6.40 mm |
405
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM CRS5001 PEI (Asia Pacific)
Transparent, Standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 3.20 mm |
405
°F @Thickness 0.126 in |
Unannealed; ASTM D648 |
|
Solvay Specialty Polymers Radel® R-5000 Polyphenylsulfone (PPSU)
Radel® R-5000 is a transparent polyphenylsulfone (PPSU) which offers exceptional hydrolytic stability, and toughness superior to other commercially-available, high-temperature engineering resins...
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 6.40 mm |
405
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® IQ420 PBT (Europe-Africa-Middle East)
Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PES GF20 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® PA6/10 GF30 TS15 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and PTFE+ Silicone LubricantFeatures: Lubricated, Heat Stabilizer and Good W..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 3.20 mm |
405
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP EF004 PEI
LNP* Thermocomp* EF004 is a compound based on Polyetherimide resin containing 20% Glass Fiber.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 3.20 mm |
405
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP QF006 PA 6/10
LNP THERMOCOMP* QF006 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 3.20 mm |
405
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10
LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 6.40 mm |
405
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® HX420HP PBT (Europe-Africa-Middle East)
Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-1, 2 |
|
Polyplastics Duranex® 3105 Polybutylene Terephthalate (PBT), Standard, 15% GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Crastin® HR5330HF BK503 Polybutylene Terephthalate (PBT)
(Unverified Data**)&
30% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate Crastin HR5330HF is a 30% glass reinforced PBT with high flow (HF) moderately toughened hydrolysis resistant (HR) resin. Excellen..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | 1/4''; ASTM D648 |
|
Ensinger TECAPEI® 10% Glass Reinforced, made from Ultem® 2100 PEI
TECAPEI™ is an amorphous thermoplastic polyetherimide (PEI) made from Sabic Innovative Plastics' Ultem® 1000 and 2000 series resins. The unreinforced 1000 series materials are translucent amber in..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-2 |
|
BASF Ultrason E 6020 P PES
Ultrason E 6020 P is an unfilled, injection molding PES grade. Polyethersulfone flakes of high molecular weight and good solubility in typical solvents (N-Methylpyrrolidone, Dimethylacetamide, Dichl..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D648 |
|
A. Schulman ComAlloy Voloy® 430 Glass Reinforced, PBT Alloy, Flame Retardant, UL
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Annealed, 0.125 in bars; ASTM D648 |
|
PolyOne Edgetek® NI-20GF/000 Nylon 6/10, Glass Filled
(discontinued **)
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Unannealed; ASTM D648 |
|
LNP Thermocomp® QF-1006 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement
(discontinued **)
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Crastin® HR5330HF BK503 PBT
(Unverified Data**)
Crastin® HR5330HF is a 30% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resis..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE
LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
207
°C @Thickness 6.40 mm |
405
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 2110N PEI
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
|
|||