- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 208 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 208 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
ASTM D648 |
|
Ovation Polymers Opnyl OP6GF33 Nylon 6, 33% Glass Reinforced, Dry
Nylon 6 - Glass reinforced (33 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ASTM D648 |
|
Oxford Polymers 20GF 20% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding
20% Glass Fiber Filled Polyetherimide for Extrusion and Injection MoldingInformation provided by Oxford Polymers.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | DAM; ISO 75-1/-2 |
|
DuPont Performance Polymers Zytel® 73G35HSL BK262 Nylon 6
(Unverified Data**)
Zytel® 73G35HSL BK262 is a 35% glass fiber reinforced, heat stabilized, black polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | |
|
Lehmann & Voss LUVOCOM® 1106-7227 Polyether imide, with carbon fiber and PTFE
Applications: High-strength and high-stiff parts; low coefficient of expansion.High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.Hig..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 6.40 mm |
406
°F @Thickness 0.252 in |
ASTM D648 |
|
Kingfa PA6-M20G16 20% Glass & 16% Mineral Filled PA6
Features:Low tendency to wrapExcellent size stabilityLow abrasionOutstanding surfaceApplications:Injection moldingAutomobile partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ISO 75-1,-2 |
|
Gromax BTG30-FN03N1 Nylon 6 30% Glass Filled (Dry)
Information provided by Gromax Enterprises Corp.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP ECL36 PEI
LNP* Lubricomp* ECL36 is a compound based on Polyetherimide resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP ECL36XXQ PEI
LNP* Lubricomp* ECL36XXQ is a compound based on Polyetherimide containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ISO 75/Af |
|
Solvay TECHNYL® C 218L V30 PA6, 30% glass fiber, Eh 0
Description: TECHNYL C 218 L V30 is a polyamide 6 reinforced with 30% glass fiber and UV stabilized.Colors: it is marketed in the natural and black color.Available in: Latin America Main Properties:..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 6.40 mm |
406
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 2100F PEI
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. US FDA and EU Food Contact Compliant, NSF 51 listing. WRAS certification in recognized col..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 2200F PEI
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 2300F PEI
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM HU2200 PEI
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM HU2310 PEI (Europe-Africa-Middle East)
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics ULTEM SF2360 PEI Blend (Asia Pacific)
High flow Ultem for thin wall application
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 407 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PBT GF30 HR BK 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightFeatures: Hydrolysis ResistantAppearance: BlackInformation provided by TP Composites, In..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA 6/12 (Asia Pacific)
LNP* Thermocomp* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 407 °F | Unannealed; ASTM D648 |
|
Techmer ES Plastiblend® PBT/ABS GF30 BK 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP PF008S PA 6
LNP THERMOCOMP* PF008S is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP WF006H PBT
LNP* THERMOCOMP* WF006H is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOTUF QX01581H PA6.10
LNP THERMOTUF* QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
208
°C @Thickness 3.20 mm |
406
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Thermocomp 2C004
LNP THERMOCOMP* 2C004 is a compound based on Ethylene Tetrafluoroethylene Copolymer resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was sup..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP PF008 PA 6 (Asia Pacific)
LNP THERMOCOMP* PF008 is a compound based on Nylon 6 resin containing Glass Fiber.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ASTM D648 |
|
Plenco 1501 Polyester, Briquette, Transfer Molded
PLENCO 01501 is a general purpose, mineral filled granular polyester molding compound, offering excellent arc and track resistance properties, low post shrinkage, and improved mechanical strength va..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ISO 75-1, 2 |
|
Polyplastics Duranex® 3216 Polybutylene Terephthalate (PBT), Standard, FR, UL approved regrind 50%, 15% GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ISO 75-1, 2 |
|
Polyplastics Duranex® CN7030 Polybutylene Terephthalate (PBT), Standard, FR, UL approved regrind 50%, 30% GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ASTM D648 |
|
A. Schulman ComAlloy Comtuf® 630 Nylon 6/6, Glass Reinforced, Impact Modified, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ASTM D648 |
|
BASF Ultramid® 8333G HI HS BK 106 33% Glass Filled PA6 (Dry)
Description Ultramid 8333G HI HS BK-102 is a 33% glass reinforced, impact modified PA6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughnes..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP JF006E PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF006E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding.
|
|||