- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 230 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 230 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
230
°C @Thickness 3.18 mm |
446
°F @Thickness 0.125 in |
Unannealed; ASTM D648 |
|
PolyOne Nymax™ ND 1233 GF Natural Polyamide 66 (Nylon 66)
The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
230
°C @Thickness 3.20 mm |
446
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
Ovation Polymers UTTAP QU BM513 GF BM Nylon, 13% Glass Reinforced
Glass reinforced (13 %) High Temperature Polyamide - Blow Molding grade with excellent chemical resistance, improved flow and high HDT. *All properties are measured after 48 hours of conditioning at..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
230
°C @Thickness 6.40 mm |
446
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics EXTEM VH1003 PEI Copolymer (Europe-Africa-Middle East)
Transparent, Thermoplastic Polyimide (TPI) resin. Glass transition Temp. (Tg) of 247°C. This resin has thinwall FR capability and has a UL94 V0 listing. Resin is RoHS compliant and halogen free acc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB SCANAMID 66 A43^E F14 Nylon 66, Glass Fiber Reinforced, Modified
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
|
Radici Radilon® WIT 30/28 Nylon 66-GF30
Automotive cooling liquid resistant PA66-GF30 grade designed to be processed by WIT technology.Information provided by Radici group.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1/-2 |
|
DSM Akulon® S223-PG2U (Dry) 13% Glass Reinforced, Impact Modified Nylon 66 (North America)
(discontinued **)&
Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | |
|
Idemitsu Kosan Xarec® EA 522 SPS, 22% Glass Filled
Crystalline Polymer, Glass Filled, Ignition Resistant, Impact Modified. Used in Electronic and Electrical applications
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
|
Kolon KOPA® KN333MT30BL Mineral Reinforced Nylon 66
MF reinforcedApplications Cam shaftsInformation provided by API-Kolon.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
>=
230
°C @Thickness 6.40 mm |
>=
446
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical LUPOY RF3208F PC, Halogen Free Flame Retardance
Description: Injection Molding, PC, Halogen Free Flame Retardance, Light Reflectance, White Color OnlyApplication: LCD Back Light Unit partsCAS: 103598-77-2 and 13463-67-1Information provided by LG ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | |
|
LATI Latamid 66 E21 G/15 PA 66, 15% Glass Fiber Reinforced
Polyamide 66 (PA66) based compound. Toughened. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
230
°C @Thickness 6.40 mm |
446
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM XH6050F PEI Copolymer
Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming. US FDA Compliant. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Unannealed; ISO 75-2/A |
|
Solvay Specialty Polymers Ixef® 1032 Polyarylamide (PARA), 60% Glass Fiber (Dry)
Ixef® 1032 is a 60% glass-fiber reinforced, general purpose polyarylamide compound which exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.Featur..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Unannealed; ISO 75-2/A |
|
Solvay Specialty Polymers Ixef® GS-1022 Polyarylamide (PARA), 50% Glass Fiber (Dry)
Ixef® GS-1022 is a 50% glass-fiber reinforced grade of polyarylamide (PARA) available in several colors. Parts molded from these colored resins can withstand high-energy gamma radiation without s..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Valox® V9260CS PET (Europe-Africa-Middle East)
Color Stable Glass filled PET
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
230
°C @Thickness 6.40 mm |
446
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM AUT230 PEI
Transparent polyetherimide (Tg 247 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
|
Polyram PlusTek PA320G3 Nylon 6.6 for Injection Molding, 15% Glass Fiber Reinforced, Flame Retardant
15% Glass fiber reinforced flame retardant Nylon 6.6 for injection molding applications.Information provided by Polyram.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 - 250 °C | 446 - 482 °F | ISO 75 A |
|
Vyncolit Vyntec® CF8030 Carbon Fiber Reinforced Novolac Phenolic
Carbon fiber reinforced phenolic moldable composite with superior tribological properties. High tensile and flexural strength and modulus combined with low density.Information provided by Vyncolit,..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-93 |
|
Wellman Wellamid® GFT33NO51-NBK2 33% Glass Fiber Reinforced, Impact Modified Nylon 66
Description: Glass Fiber Reinforced, Impact Modified Nylon 66Information provided by Wellman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-93 |
|
Wellman Wellamid® GSF25/15-66 22L-NBK1 40% Glass Sphere/Fiber Reinforced Nylon 66
Description: Glass Sphere/Fiber Reinforced Nylon 66Information provided by Wellman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 179 |
|
CP-Polymer-Technik Wellamid® 6600 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 66, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
|
Eurostar Star X 1615 33V S4 PA66, Glass Fiber Reinforced, UV stabilized, Injection Molding
Star X 1615 33V S4 is an Impact Modified, Glass Fiber Reinforced, UV stabilized Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
|
Eurostar Staramide AG3K PA66, 15% Glass Filled, Injection Molded
AG3K is a Heat and Hydrolytically Stabilized, 15% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppl..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
|
Eurotec® Tecomid® NA40 GR14 NL MC PA6.6, 14% glass fiber reinforced, impact modified, heat stabilized, natural
Information provided by Eurotec®
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
|
E-Polymers TEKAMID® TA210M40 , 40% Mineral Filled PA66, DAM
40% Mineral filled, Heat resistance, PlatableInformation provided by E-Polymers Co. Ltd.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-2/AF |
|
Addiplast Addinyl C2 ZV15 Nylon 66/6, 15% Glass Filled
Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
|
Beijing Chemical Industry KAIFA® MN201-G20 Nylon 66 Resin
20% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-2/AF |
|
Addiplast Addinyl C2 ZV30 Nylon 66/6, 30% Glass Filled
Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
|
Polyram PlusTek RA320G5 Nylon 66 for Injection Molding, 25% Glass-Fiber Reinforced, Flame Retardant and High Stiffness
25% Glass-fiber reinforced, flame retardant and high stiffness Nylon 66 for injection molding applications.Information provided by Polyram.
|
|||