- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 239 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 239 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® HFD1014 PC Copolymer (Europe-Africa-Middle East) 7 MFR LEXAN HFD Copolymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® SLX2432D PC Copolymer (Asia Pacific) Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. V2 rated. Available in diffusion colors.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer (Europe-Africa-Middle East) 40 MFR LEXAN High Flow Ductile Copolymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ASTM D648 |
| LATI LATAN 13 Medium Viscosity Polyoxymethylene Copolymer (POM)
(Unverified Data**) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ASTM D648 |
| Custom Resins Duratel™ MF13 Acetal Copolymer
(discontinued **) Description: Duratel™ MF13 is a 13 melt flow, general purpose acetal copolymer. Information provided by Custom Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 4.00 mm |
239 °F @Thickness 0.157 in |
after annealing 150°C 16 hr; ASTM D648 |
| Solvay Specialty Polymers Solef® 3208/0150 Anti-friction PVDF Compound
(discontinued **) Key features of this grade: Anti-friction, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crysta.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75-1,-2 |
| Ineos ABS Lustran® ABS 150G22 20% Glass Fiber Reinforced Grade |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® MX 1002 Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | |
| LATI Latan 13 S/20 POM, 20% Glass Bead Reinforced Polyoxymethylene (POM) based compound. Glass beads. Medium viscosity. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL STN15HF PPE+PS Automotive interiors. Improved flow characteristics/overall processing economy. 240F DTUL. High impact/good property retention after heat ageing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL STN15HF PPE+PS (Asia Pacific) Automotive interiors. Improved flow characteristics/overall processing economy. 240F DTUL. High impact/good property retention after heat ageing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics NORYL V01525 PPE+HIPS (Asia Pacific) Noryl* V01525 is a 15% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics NORYL V01525 PPE+HIPS (Europe-Africa-Middle East) Noryl* V01525 is a 15% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ASTM D648 |
| Samyang Triloy® 170 PC/PBT alloy Characteristics:Impact resistantChemical resistantDimensional stabilityProcessabilityFlame retardantApplications:Automotive bumperAutomotive outdoor handleAll information provided by Samyang |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL N225Z PPE+HIPS (Asia Pacific) PPE+PS 115deg,C, FR V-0 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP D7002IXH PC LNP* THERMOCOMP* D7002IXH is a compound based on Polycarbonate siloxane copolymer resin containing proprietary antimicrobial additives. Designed for touch surfaces, housings, etc., in healthcare an.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ASTM D648 |
| Shinkong Synthetic Fibers Shinite® PP4220 PP, High Impact, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Noryl EN130S PPE+HIPS (Europe-Africa-Middle East) Noryl EN130S is an extrusion grade with a Vicat B/120 temperature of 140 deg C, developed for profile extrusion and in compliance with Food contact regulations; color limited.This data was supplied .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | 0.25 inch; ASTM D648 |
| PlastxWorld CEVIAN® S3500 PC/ABS alloy Flame retarded PC/ABS Alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| Covestro Bayblend® KU 2-1514 BBS073* Polycarbonate + ABS, Flame Retardant Grade Developmental productHigh heat resistant injection molding gradeimproved chemical resistance and stress cracking behavior compared to KU 2-1514ball indentation temperature = 125 °CVicat/B 120 tempe.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT3Z black 9564 PA* Product description: Grivory HT3Z is an unreinforced and impact resistant, engineering thermoplastic based on semi crystalline partially aromatic copolyamide. This Grivory HT product is partially ba.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
| Diamond Polymers ABS TX-541 Description: Super High Heat ABSInformation provided by Diamond Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® TR 90 LS PAMACM12 Product description: Grilamid TR 90 LS natural is a high purity transparent thermoplastic polyamide, based on aliphatic and cycloaliphatic monomers. Grilamid TR 90 LS natural contains a processing a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | |
| Arkema Group Lucalor® PEY 221 CPVC, Pipe Grade LUCALOR PEY 221 is a chlorinated polyvinyl chloride compound (CPVC) developed for the extrusion of pipes for hot water supply and distribution systems.ISO data provided by the manufacturer, Arkema. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | DIN EN ISO 75-2/Ae |
| BASF Elastollan R 2000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ASTM D648 |
| Custom Resins Duratel™ MF9 Acetal Copolymer
(discontinued **) Description: Duratel™ MF9 is a 9 melt flow, general purpose acetal copolymer. Information provided by Custom Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics NORYL PX2391 PPE+HIPS (Europe-Africa-Middle East) PX2391 is a 10% glass fiber reinforced, heat stabilized, low odor and low emission NORYL(R) grade for interior automotive applications, especially instrument panels |
|||