- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 244 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 244 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 3.20 mm |
244
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CH6310 PC+ABS (Asia Pacific)
CH6310 is a high heat, high flow PC/ABS resin, with nonbrominated, nonchlorinated flame retardant system. All color available.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Cycoloy® XCM830 PC+ABS
PC/ABS with high stiffness and impact performance
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Cycoloy® XCM830 PC+ABS (Europe-Africa-Middle East)
PC/ABS with high stiffness and impact performance
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer (Asia Pacific)
This product will be phased out per January 2015 -- Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm, opaque polycarbonate copolymer resin with improved scratch resistance.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer (Europe-Africa-Middle East)
Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East r..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® EXL1493T PC Copolymer
Lexan* EXL1493T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance, with mold release. This resin offers excellent low temperature (-3..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® FXE1414L PC Copolymer (Europe-Africa-Middle East)
Opaque EXL, UV-Stabilized & light shielding capability (Wall thickness >0.8mm), for portable electronics device enclosure application. Only available in white, grey and limited pastel colors. Consul..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® HPX4 PC Copolymer
Medium flow specialty polycarbonate - improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® HPX4 PC Copolymer (Asia Pacific)
Medium flow specialty polycarbonate - improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® HPX4R PC Copolymer (Europe-Africa-Middle East)
Medium flow specialty polycarbonate with outstanding processability, ductility and autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatib..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® HPX4REU PC Copolymer (Europe-Africa-Middle East)
Medium flow specialty polycarbonate - improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 6.40 mm |
244
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® ML6413 PC
Lexan* ML6413 resin is an impact modified, flame retardant polycarbonate grade with Br- & Cl-free FR systems. It features improved light shielding capability with good flow, impact and thermal prope..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 6.40 mm |
244
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® ML6413 PC (Europe-Africa-Middle East)
Lexan* ML6413 resin is an impact modified, flame retardant polycarbonate grade with Br- & Cl-free FR systems. It features improved light shielding capability with good flow, impact and thermal prope..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 3.20 mm |
244
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® SLX2432D PC Copolymer (Europe-Africa-Middle East)
Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. V2 rated. Available in diffusion colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East reg..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 4.00 mm |
244
°F @Thickness 0.157 in |
Unannealed; ISO 75-2 |
|
NOVA Chemicals Dylark® 510XT Glass Reinforced Engineering Resin
Features: Higher toughness product, Excellent stiffness, High heat resistance, Superior adhesion to urethane foamApplications: Instrument panel substrates, Mid-Consoles, Center Stacks, Interior tri..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 3.20 mm |
244
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL PX9406P PPE
NORYL* PX9406P resin is an FR (non-halogenated) grade potentially suitable for a variety of electronics applications. RTI (impact) = 105 C. F1 listed in BK color.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 3.20 mm |
244
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS
LNP* LUBRICOMP* ZP001XXP is a compound based on PPE+PS resin containing 5% PTFE/Silicone. Added features of this material include: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 3.20 mm |
244
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS (Asia Pacific)
LNP* Lubricomp* ZP001XXP is a compound based on PPE+PS Blend resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 3.20 mm |
244
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RF006LXP PA 66 (Asia Pacific)
LNP* Thermocomp* RF006LXP is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Low Extractible.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 3.20 mm |
244
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RZ006SXP PA 66 (Asia Pacific)
LNP* Thermocomp* RZ006SXP is a compound based on Nylon 66 resin containing Milled Glass.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics NORYL NH5120 PPE+PS
Noryl* NH5120 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated V1 flame re..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | ASTM D648 |
|
Westlake Plastics PVDF Film Made from KYNAR® Polyvinylidene Fluoride Resin
Excellent chemical resistance. Stable to UV and the effects of weather. Low NBS smoke generation and superior LOI. Excellent transmittance of solar energy. Excellent dielectric strength. High h..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | annealed; ISO 75 |
|
Chi Mei Polylac® PA-777E ABS - High Heat
Ultra High Heat
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | ASTM D648 |
|
Ensinger DELRIN® 100AF Acetal Homopolymer, 13% PTFE filled (POM)
Ensinger’s DELRIN®100AF blend stock shapes are a 13% PTFE fiber filled homopolymer acetal. They offer an improved coefficient of friction, better lubricity, and improved wear characteristics over ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | |
|
BASF Luranyl® KR 2452/3 Polyphenylene Ether + Styrene-Butadiene Blend
This grade, which contains a halogen-free flame-retardant, is especially resistant to heat deformation. Applications include: functional electrical parts (e.g. switches, transformer housings, defle..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | ISO 75 |
|
Ascend Performance Materials Vydyne® R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded
Vydyne® R220 is a 40% mineral reinforced Nylon 66 resin formulated for improved impact strength. Also available in black as R228. It is an injection molding grade formulated to retain the inherent ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Unannealed; ISO 75-2/A |
|
Ascend Performance Materials Vydyne® R228 Nylon 66, 40% Mineral Reinforced, DAM
Vydyne® R228 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in black, it is an injection-molding grade formulated to retain the inherent processing advant..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | ASTM D648 |
|
A. Schulman ComAlloy Hiloy® 263 Glass Reinforced, Modified SMA
Data provided by the manufacturer, ComAlloy International Company.35% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Delrin® 577 BK000 Acetal Homopolymer
(Unverified Data**)
Delrin® 577 BK000 is a medium viscosity acetal homopolymer containing 20% glass fiber filler, with high stiffness, low warpage and low creep for superior performance at elevated temperature. It con..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
118
°C @Thickness 6.40 mm |
244
°F @Thickness 0.252 in |
ASTM D648 |
|
Kingfa JE2-R2G30 Glass Fiber Reinforced ABS/PBT Alloy
Features:High stiffness, high hardnessGood mechanical strengthGood chemical resistanceGood size stabilityGood heat stabilityLow tendency to warpApplications:Optical appliance (camera, video)Sports a..
|
|||