- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 248 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 248 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Unannealed; ISO 75-2 |
|
PolyOne Nymax™ GF 1200 A 55 HS Black 13 Polyamide 66 (Nylon 66)
The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
248
°C @Thickness 6.40 mm |
478
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical LUMID GP2251BF PA66+GF25%, Flame Retardant
Feature: Injection Molding, PA66+GF25%, Flame RetardantApplication: IT/OA (Micro Switch)CAS No. 32131-17-2, 65997-17-3, 88497-56-7, 1309-64-4 and 138265-88-0Information provided by LG Chemical
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
248
°C @Thickness 6.40 mm |
478
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical LUMID LW4403B(W) PA66+GF/MF40%, Low Warpage
Feature: Injection Molding, PA66+GF/MF40%, Low WarpageApplication: Automotive PartsCAS No. 32131-17-2, 13983-17-0 and 65997-17-3Information provided by LG Chemical
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | ASTM D648 |
|
Kolon KOPA® KN333G35CR G/F Reinforced Nylon 66
High thermal resistant, Weather resistant, dimensionally stableApplications Cylinder head coversInformation provided by API-Kolon.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP OCP36A PPS - Branched
LNP* LUBRICOMP* OCP36A is a compound based on PPS - Branched resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant, Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP OCP36A PPS - Branched (Asia Pacific)
LNP* Lubricomp* OCL-4536 is a compound based on PPS - Branched resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Internally Lubricated, Electrically Conductive..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
248
°C @Thickness 3.20 mm |
478
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP RFG16S PA 66
LNP* LUBRICOMP* RFG16S is a compound based on Nylon 66 resin containing 5% Graphite, 30% Glass Fiber. Added features of this material include: Heat Stabilized, Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP RFL36XXZ PA 66 (Asia Pacific)
LNP Lubricomp is a compound based on PA66 resin containing glass fiber, PTFE. It is an internally lubricated compound that provide excellent chemical resistance, strength and wear/friction propertie..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
248
°C @Thickness 3.20 mm |
478
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP RFN169 PA 66
LNP* LUBRICOMP* RFN169 is a compound based on Nylon 66 containing 30% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant, Flame Retardant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
248
°C @Thickness 3.20 mm |
478
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP RFP38 PA6.6
LNP* LUBRICOMP* RFP38 is a compound based on Nylon 66 containing 40% Glass Fiber, 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
248
°C @Thickness 3.20 mm |
478
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Lubricomp UCL24S PPA (Asia Pacific)
LNP* Lubricomp* UCL24S is a compound based on Polyphthalamide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Heat Stabilized, Electrically Cond..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Unannealed; ISO 75-2/A |
|
Solvay Specialty Polymers Omnix® FC-9050 Polyamide, High Performance (HPPA), 50% Glass Fiber
Omnix® FC-9050 is a 50% glass-fiber reinforced high-performance polyamide. It is hot-water moldable and intended for use in components requiring superior mechanical properties even after moisture..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Unannealed; ISO 75-2/A |
|
Solvay Specialty Polymers Xydar® MG-850 Liquid Crystal Polymer (LCP), 50% GlassMineral
Xydar® MG-850 liquid crystal polymer (LCP) is a 50% glass/mineral reinforced injection molding grade developed for electrical/electronic applications utilizing surface mount technology. The mater..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-KON RE006 PA 66
LNP STAT-KON* RE006 is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | ASTM D648 |
|
Samyang Tramid® 210G15 Polyamide, Reinforced
Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210G15 is a reinforced grade.Applications:Automotive gear level housingConnectors..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
248
°C @Thickness 3.20 mm |
478
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RF003AXH PA 66
LNP* THERMOCOMP* RF003AXH is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material includes: Healthcare.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics LNP Thermocomp RF0069 PA 66 (Europe-Africa-Middle East)
Flame retarded, 30% glass fibre reinforced Polyamide 66 injection moulding resin.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
>=
248
°C @Thickness 3.20 mm |
>=
478
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Thermocomp UC008S PPA (Asia Pacific)
LNP* Thermocomp* UC008S is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | ASTM D648, ISO 75 |
|
EPICHEM Epinyl PA 66 GF 30 H Polyamide 66, 30% Glass, Heat Stabilized
Characteristics: 30% glass fibre filled
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | ASTM D648, ISO 75 |
|
EPICHEM Epinyl PA 66 GF 30 Polyamide 66, 30% Glass
Characteristics: 30% glass fibre filled
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | DAM; ISO 75-1/-2 |
|
DuPont Performance Polymers Zytel® 70G30HSL NC010 Nylon 66
(Unverified Data**)
30% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G30HSL NC010 is a 30% glass fiber reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Perform..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
|
Eurostar Staramide AG6H PA66, 30% Glass Filled, Injection Molded
AG6 is a Heat Stabilized, 30% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
|
Eurostar Staramide RF006SXP PA66, 30% Glass Fiber Filled, Injection Molded
Staramide RF006SXP is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as RF1006HS)Information provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
|
Eurostar Starflam AFR450X2 PA66, 25% Glass Filled, Injection Molded
AFR450X2 is a Red Phosphorous, Flame Retardant, 25% Glass Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive su..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
|
Eurostar Starflam AFR470X2 PA66, 35% Glass Filled, Injection Molded
AFR470X2 is a Red Phosphorous, Flame Retardant, Glass Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppli..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
|
Eurostar Starflam RF0069 PA66, 30% Glass Fiber, Flame Retardant, Injection Molded
Starflam RF0069 is a Flame Retardant, 30% Glass Reinforced Polyamide 66 Injection Molding Resin (also known as PA66 30V U2 Z79 or RF1006Z590)Information provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
|
Eurostar Starflam AFR460B PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding
Starflam AFR460B is a Flame Retardant, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | ASTM D648 |
|
A. Schulman ComAlloy Lubrilon® 637 Nylon 6/6, Carbon Fiber/Molybdenum Disulfide Filled
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-KON OE003A PPS - BRANCHED (Europe-Africa-Middle East)
LNP* STATKON* OE003A is a compound based on PPS ( branched ) resin containing Carbon Fiber. Added features include: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
248
°C @Thickness 3.20 mm |
478
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP VERTON RV00CEXS PA 66
LNP* VERTON* RV00CEXS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural.
|
|||