- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 248 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 248 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 943X PC Copolymer (Asia Pacific)
Lexan* 943X is a UV stabilized medium flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low tempera..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® CFR5630 PC COPOLYMER
LEXAN™ CFR5630 Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density an..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer
Lexan* EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® EXL1494T PC Copolymer
Lexan* EXL1494T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers extreme low temperature (-40 C) ductility in comb..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® EXL1810T PC Copolymer (Asia Pacific)
Lexan* EXL1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers cold temperature (0 °C) ductility in combination with very high flow char..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® FXE1810T PC Copolymer
Lexan* FXE1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection moldable grade. This specialty PC offers excellent processability, very high flow and improved ductility charac..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® FXM1413T PC Copolymer
PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® FXM1413T PC Copolymer (Europe-Africa-Middle East)
PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.This data was supplied by ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HPXS8R PC Copolymer
Very high flow specialty polycarbonate with outstanding processability and ductility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 o..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® LUX7432C PC COPOLYMER (Europe-Africa-Middle East)
Lexan* LUX7432C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm a..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® LUX7436C PC COPOLYMER (Europe-Africa-Middle East)
Lexan* LUX7436C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm a..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® LUX9136C PC COPOLYMER (Asia Pacific)
Lexan* LUX9136C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® SLX1432 PC Copolymer
Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. Available in opaque colors. Typical minimum color tolerance limit is DE CMC < 1.0
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
|
LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**)
Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® BFL2000U PC (Europe-Africa-Middle East)
Lexan* BFL2000U Polycarbonat (PC) resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating. Lexan* BFL2000U is designed for hig..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 6.40 mm |
248
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® FL3000 PC (Asia Pacific)
Structural foam: 10% weight reduction at 0.250" wall. ECO-conforming. Impact modified PC with excellent low-temperature impact and UV-stability.This data was supplied by SABIC-IP for the Asia Paci..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® FXE1414T PC Copolymer (Europe-Africa-Middle East)
Clear PC-siloxane copolymer with excellent processability, for Visual fX capability in "Energy" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color packa..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75 |
|
GEHR Plastics POM-10PE Acetal Copolymer
Polyoxymethylene can be used in temperatures up to 100°C. The high surface strength is only surpassed by a few materials. POM shows good sliding properties and high resistance to wear and tear be..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
|
Lavergne VYTEEN PC/ABS 8515XF Polycarbonate - Acrylonitrile Butadiene Styrene Alloy
Vyteen PC/ABS 8515XF is an enhanced PC/ABS alloy with balanced impact/stiffness properties designed for injection molding applications.Features: -High resilience -Excellent processability -High d..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | V-notch; ISO R 75 |
|
Schwartz Technical Plastics LAMIGAMID® 317 Cast Polyamide 6, Heat Stabilized, Conditioned
Application: coupling parts, sealing rings, bearingsInformation provided by Schwartz Technical Plastics GmbH
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® POM CO GF5 CC 5% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforced, 5% Filler by WeightFeatures: Copolymer and Chemically CoupledInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL PN275 PPE+PS
PPE+PS with low mineral loading. High heat, platable applications.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
120
°C @Thickness 3.20 mm |
248
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL PN275F PPE+PS
PPE+PS with low mineral loading. High heat, platable applications. NSF approved for water contact applications.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
|
A. Schulman POLYFLAM™ FCB 1236-8555 General Purpose Homopolymer Polypropylene
DescriptionPolyfort® FCB 1236-8555 is a general purpose homopolymer polypropylene filled with 20% glass fiber.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | 120°C/hr; ASTM D 648 |
|
Cossa Polimeri ESTAPROP H 0540 GFC Polypropylene, 20% Glass Filled
PP homopolymer 20% chemically coupled glass fiber reinforcedInformation provided by Cossa Polimeri S.r.l.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75-1/2 |
|
Eurotec® Tecomid® NB40 MR30 NL PA 6 30% mineral reinforced
Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
|
Asahi Kasei Tenac®-C EF750 Acetal Copolymer, Antistat
(discontinued **)
Antistatic grade containing special carbon black.Applications: Parts requiring antistatic properties.This product is not a part of the standard product line dated 2003.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
|
A. Schulman POLYFLAM™ FCB 1236-8555 General Purpose Homopolymer Polypropylene
DescriptionPolyfort® FCB 1236-8555 is a general purpose homopolymer polypropylene filled with 20% glass fiber.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Annealed; ASTM D648 |
|
Solvay Specialty Polymers Amodel® ET-1000 HS Polyphthalamide (PPA)
(Unverified Data**)
Amodel ET-1000 HS is an impact modified, heat stabilized polyphthalamide (PPA) that exhibits exceptional impact strength and toughness. Like all Amodel PPA resins, ET-1000 HS offers high fatigue str..
|
|||