- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 249 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 249 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D-648 |
|
PlastiComp Velocity® LCF50-PA6 High Flow Nylon 6, 50% Long Carbon Fiber
This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
|
Niche Polymer PA66GF43BK Nylon 66, 43% Glass Fiber Filled
Information provided by Niche Polymer
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
249
°C @Thickness 3.20 mm |
480
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP RFL36U PA 66
LNP* LUBRICOMP* RFL36U is a compound based on Nylon 66 resin containing 15% PTFE, 30% Glass Fiber. Added features of this grade include: Wear Resistant, UV Stabilized.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6/6 GB40 HS BK 40% Glass Bead Filler
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 40% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearance: BlackInforma..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6/6 GF33 HS L BK001 33% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® PA6/6 CF30 TL12 30% Carbon Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE + Silicone Lubricant(15%)Features: Lubricated and Good Wear ResistanceTPCI# 6466101Inf..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
|
Techmer ES Plastiblend® PPS 05003
Availability: North AmericaForms: Pellets Additive: Lubricant and Strontium Ferrite Features: LubricatedUnoriented Magnetic:Residual Induction, BR: 1100 GaussCoercive Force, Hc: 750 OerstedsIntrinsi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
249
°C @Thickness 3.20 mm |
480
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP VF008A PA 66
LNP* THERMOCOMP* VF008A is a compound based on High Impact Nylon 66 containing 40% Glass Fiber.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
|
Plastics Group Polifil® 628-33GF Glass Fiber-Reinforced Nylon 6/6 (DAM)
Polifil® GFN/MRN 6/6 reinforced series of compounds offer superior strength, rigidity and creep resistance. Glass fibers provide excellent thermal and dimensional stability while maintaining good h..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ISO 75 |
|
Polyram PlusTek RA331G6 Nylon 66 for Injection Molding, 30% Glass-Fiber Reinforced
30% Glass-fiber reinforced Nylon 66 for injection molding applications.Information provided by Polyram.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
|
Ashley Polymers Ashlene® 528L-33G Nylon 66, 33% Glass Reinforced
General purpose glass fiber reinforced Nylon 66, designed for parts requiring excellent thermal and dimensional stability and higher strength than conventional resins.Data provided by the manufactur..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D-648 |
|
PlastiComp Complet® LGF30 - PA66 Nylon 66, 30% Long Glass Fiber Reinforced
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 30% long glass fiber reinforcementInformation provided by PlastiComp, In..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
|
E-Polymers SEPAZ® LA30 PA66 LFT Resin
Long Fiber Thermoplastics: SEPAZ LFT products, injection moldable long fiber-reinforced thermoplastics (LFT), are made using a unique pultrusion that thoroughly wets out the glass fibers and deliver..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-KON REF42 PA 66 (Asia Pacific)
LNP* Stat-kon* REF42 is a compound based on Nylon 66 resin containing Glass Fiber, Carbon Fiber.
|
|||