- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 253 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 253 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ISO 75, ASTM D648 |
|
Nilit Nilamid A3 H G7 General Purpose 35% Glass Reinforced PA66
Description: Nilamid A3 H G7 is a general purpose 35% glass fiber reinforced NYLON 66 that gives an excellent combination of tensile strength, stiffness and impact strength. It is one of the most wi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | DAM; ISO 75-1/-2 |
|
DuPont Performance Polymers Zytel® 70G30L NC010 Nylon 66
(Unverified Data**)
Zytel® 70G30L NC010 is a 30% glass fiber reinforced polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 6.40 mm
|
487
°F <br>@Thickness 0.252 in
|
ASTM D648 |
|
Kingfa PA66-G50 50% Glass Fiber Reinforced PA66
Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP REL22 PA 66
LNP* LUBRICOMP* REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP RFL26S PA 66
LNP* LUBRICOMP* RFL26S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 488 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill FR® PA6/6 GF25 FR BK 25% Glass Filled (Dry)
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 25% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Heat Stabilized and LubricatedAppear..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 488 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® PA6/6 CF30 TL15 HS BK 30% Carbon Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%) and Heat StabilizerFeatures: Lubricated, Good Wear Resistance, Heat Sta..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM D648 |
|
Samyang Tramid® 210G35 Polyamide, Reinforced
Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210G35 is a reinforced grade.Applications:Automotive gear level housingConnectors..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RC008 PA 66
LNP THERMOCOMP* RC008 is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RF008 PA 66 (Asia Pacific)
LNP Thermocomp RF008 is a compound based on PA66 resin containing glass fiber. It is used in many applications requiring high strength over weight performance. Also known as Thermocomp RF-1008
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RX09411H PA 66
LNP* Thermocomp* RX09411H is a compound based on Nylon 66 containing Proprietary Fillers. Characteristics are: Radiopacity and Healthcare.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON REF42 PA 66
LNP* STAT-KON* REF42 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON REF42I PA 66
LNP* STAT-KON* REF42I is a compound based on Nylon 6/6 containing Proprietary Fillers. Added feature of this grade is: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RF008XXH PA 66
LNP* THERMOCOMP* RF008XXH is a compound based on Nylon 66 resin containing 40% Glass Fiber. Added feature of this material includes: Healthcare.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RX05494 PA 66
LNP* Thermocomp* RX05494 is a compound based on Nylon 6/6 resin containing glass fiber fillers. Added features of this material include: Heat Stabilized.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66
LNP* Thermocomp* RX98372H is a compound based on Nylon 66 resin containing Proprietary Fillers. Characteristics of this grade are: Healthcare.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66
LNP* Thermocomp* RX98372H is a compound based on Nylon 66 resin containing Proprietary Fillers. Characteristics of this grade are: Healthcare.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP VERTON RV00AE PA 66 (Europe-Africa-Middle East)
LNP* VERTON* RV00AE is a compound based on PA 66 rsin containing Long Glass Fiber. Added features include; Easy Molding.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP VERTON RX07013 PA 66 (Europe-Africa-Middle East)
LNP VERTON * RX07013 is a compound based on Nylon 66 resin containig Long Glass. Added features of this material include: Easy Molding and UV Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP VERTON RX89047 PA 66
LNP* VERTON* RX89047 is a compound based on Nylon 66 resin containing Proprietary Fillers. Added feature of this grade is: Structural.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP VERTON RX89047 PA 66 (Asia Pacific)
LNP* Verton* RX89047 is a compound based on Nylon 66 resin.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ISO 75 |
|
Polyram Polytron A60N01 Nylon 6.6, 60% Long Fiber Glass
60% Long fiber glass reinforced natural Nylon 6.6, heat stabilized, for injection molding.Information provided by Polyram.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | DAM; ISO 75-1/-2 |
|
DuPont Performance Polymers Zytel® 70G30HSLR BK099 Nylon 66
(Unverified Data**)
30% Glass Reinforced Heat Stabilized Hydrolysis Resistant Polyamide 66 Zytel 70G30HSLR BK099 is a 30% glass fiber reinforced heat stabilized hydrolysis resistant polyamide 66 resin for injection mol..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM D648 |
|
Ashley Polymers Ashlene® 527LD-45LG Nylon 66, 45% Long Glass Fiber Reinforced
Long glass fiber reinforced impact modified Nylon 66, designed for parts requiring excellent thermal and dimensional stability and higher strength than available with conventional glass reinforced r..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM D648 |
|
A. Schulman ComAlloy Lubrilon® 632 Nylon 6/6, Carbon Fiber/PTFE Filled
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ISO 75 |
|
Polyram Polytron A50B01 Nylon 6.6, 50% Long Fiber Glass
50% Long fiber glass reinforced black Nylon 6.6, heat stabilized for injection molding applications.Information provided by Polyram.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM-D648 |
|
Polyram Polytron A50N02 Nylon 66, Chemically Coupled 50% Long Fiber
A CHEMICALLY COUPLED 50% LONG FIBER GLASS REINFORCED NATURAL NYLON 6.6 HEAT STABILIZED, UV STABILIZED FOR INJECTIONInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM D648 |
|
A. Schulman ComAlloy Hiloy® 653 Nylon 6/6, Carbon Fiber Reinforced, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
253
°C <br>@Thickness 3.20 mm
|
487
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP VERTON RX00327 PA 66
LNP* VERTON* RX00327 is a compound based on Nylon 66 resin containing proprietary fillers. Added feature of this material is: Structural.
|
|||