- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 271 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 271 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | |
|
Plastcom SLOVALEN PH 76 T 20 FRD 5 PP, 20% mineral filling, flame retardant
FeaturesModified homopolymer PP for injection moulding, with the content of 20% microground chemically modified talc, retarded with halogen flame retardant Application - electrical industry - termin..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® FXG154 PC
FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® SLX2231D PC Copolymer
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Diffusion colors.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® SLX2231D PC Copolymer (Asia Pacific)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Diffusion colors.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® SLX2231T PC Copolymer (Asia Pacific)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® SLX2231T PC Copolymer (Europe-Africa-Middle East)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Europe-Africa-..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® SLX2271T PC Copolymer (Europe-Africa-Middle East)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL36P PC
LNP* Lubricomp* DFL36P is a compound based on Polycarbonate containing 30% Glass Fiber 15% PTFE. Added features include: Exceptional Processing. Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL36P PC
LNP* Lubricomp* DFL36P is a compound based on Polycarbonate containing 30% Glass Fiber 15% PTFE. Added features include: Exceptional Processing. Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP ZFL34 PPE+PS
LNP* LUBRICOMP* ZFL34 is a compound based on PPE+PS resin containing 20% Glass Fiber, 15% PTFE. Added feature of this gradae is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON DX98477 PC
LNP* STAT-KON* DX98477 is a compound based on Polycarbonate containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC (Asia Pacific)
LNP* THERMOCOMP* DFZ22P is a compound based on Polycarbonate resin containing Glass Fiber, Milled Glass. Added features of this material include: Exceptional Processing.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP MFB63 PP (Europe-Africa-Middle East)
LNP* THERMOCOMP* MFB63 is a compound based on Polypropylene resin containing Glass Bead, Glass Fiber.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
Samyang Trirex® 3020IR Polycarbonate with Heat Stabilizer
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020IR is a high flow grade with added heat stabilizers, separating materials and stain..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
Samyang Trirex® 3020PJ Polycarbonate
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020PJ is a high flow grade.Information provided by Samyang.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
Samyang Trirex® 3020U UV Stable Polycarbonate
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020U is a high flow, UV Stable grade.Information provided by Samyang.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP (Asia Pacific)
30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Thermocomp MF006S PP (Asia Pacific)
LNP* Thermocomp* MF006S is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia P..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | 0.125";; ASTM D648 |
|
Diamond Polymers PC 0614UV UV Stabilized Polycarbonate
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | |
|
Aclo Accutech Polypropylene Homopolymer HP0336G20M10CL Glass/Mineral Reinforced Coupled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
A. Schulman ComAlloy Comtuf® 106 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled, Impact Modified, UL
Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
A. Schulman ComAlloy Lubrilon® 511 Polycarbonate, Glass Fiber/PTFE, UL
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® FXG154 PC (Asia Pacific)
FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® ML6230 PC Copolymer
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. Available in transparent and tinted colors.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® ML6230 PC Copolymer (Asia Pacific)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. Available in transparent and tinted colors.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® ML6230 PC Copolymer (Europe-Africa-Middle East)
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. Available in transparent and tinted colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
133
°C <br>@Thickness 3.20 mm
|
271
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP VERTON NV004E PC+ABS (Asia Pacific)
LNP VERTON* NV004E is a compound based on PC+ABS Blend resin containing Long Glass. Added features of this material include: Easy Molding.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
|
Samyang Trirex® 3020R Polycarbonate with Heat Stabilizer
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020R is a high flow grade with added heat stabilizers and separating materials.Informa..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP Stat-kon DE006P PC (Europe-Africa-Middle East)
LNP* Stat-kon* DE006P is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-KON DX04490 PC (Asia Pacific)
LNP* Stat-kon* DX04490 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive.
|
|||