- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 302 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 302 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO.75 DIN.53461 (dry sample) |
|
Omnia Plastica Rilsan® PA6 GF - Akulon GF - at 50% RH
Polyamide 6 reinforced with the addition of 30% glass fibre and graphite. The glass charge makes the material highly resistant to abrasion, compression and flexing. Akulon GF is particularly suitabl..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75-1/-2 |
|
Quadrant EPP Ertalon® 66 GF30 PA 66, 30% glass filled, extruded (ISO Data)
Compared with virgin PA 66, this 30 % glass fibre reinforced and heat stabilised nylon grade offers increased strength, stiffness, creep resistance and dimensional stability whilst retaining an exce..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB SCANMID 6 B12^ FX30 Nylon 6, Glass Fiber Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® FXM4701 PPC
LEXAN FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.This data was supplied by SABIC-IP for the Americas ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75 |
|
Gharda Chemicals GATONE™ 5400 PEEK, Medium Viscosity Grade
(discontinued **)
Medium viscosity grade for extrusion and injection moldingCHARACTERISTICS: Outstanding chemical resistance.Outstanding wear resistance.Outstanding resistance to hydrolysis.Excellent mechanical prope..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75 |
|
Gharda Chemicals GATONE™ 5600 PEEK, Low Viscosity Grade
(discontinued **)
Low viscosity. grade for injection molding of thin sections & complex partsCHARACTERISTICS: Outstanding chemical resistance.Outstanding wear resistance.Outstanding resistance to hydrolysis.Excellen..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® FXM4701 PPC (Europe-Africa-Middle East)
LEXAN FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.This data was supplied by SABIC-IP for the Europe-Af..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
Asahi Kasei Tenac® GT525 Acetal Homopolymer, 25% Glass Beads
(discontinued **)
25% glass beads-filled grade with superior isotropic dimensional stability.Applications: Speedometer frames.This product is not a part of the standard product line dated 2003.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
LG Chemical LUCEL GB-325 Low Warpage POM, 25% Glass Bead Filled
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | |
|
LATI Latilub 80-40GRT PPS, Graphite/PTFE Filled
Self-lubricating product based on Polyphenylene Sulfide (PPS). Graphite / PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Ind..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Unannealed; ASTM D648 |
|
Techmer ES Plastiblend® PA6/ABS 1120 GF20 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedAppearance: Natural ColorInformation p..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
150
°C @Thickness 3.20 mm |
302
°F @Thickness 0.126 in |
Unannealed; ASTM D648 |
|
Teknor Apex Sinpolene GPP1640 Polypropylene
Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 40% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
Unitika P-5001 Engineering Plastic
P series resins are resins succeeding the characteristics of the neat polymer, U100, and improved in flowability and optical properties. Among many super engineering plastics, the resins are few tra..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | GB1634 |
|
Zhejiang Juner PA66-301-G10 Flame-Retardant & Glass Reinforced, Environmental PA66
Applications: Electric Appliance PedestalInformation provided by Zhejiang Juner New Materials Co, Ltd.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Absolute Drying; ASTM-D648 |
|
Toyobo GLAMIDE® T-777-02 Nylon-6
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene
DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM-D648 |
|
Polyram Polytron P35B03 Copolymer Polypropylene, Chemically Coupled 35% Long Glass Fiber
A CHEMICALLY COUPLED 35% LONG GLASS FIBERS REINFORCED BLACK POLYPROPYLENE, HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | |
|
Covestro Apec® HT KU 1-9341 High-Heat Polycarbonate
Transparent and opaque shades possible.Applications: Lighting, automotive and household goods, light covers, indicator and brake light lenses.Information provided by Bayer.As of 1 September 2015, Ba..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
|
Eurostar Starpylen MX06050 PP, 30% Glass Filled, Injection Molded
Starpylen MX06050 is a 30% Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75-2 |
|
CENTROPLAST CENTROMID 6.6 GF 30 Polyamide 6.6 30% glass fiber
This material has very high strength and rigidity, with lower moisture absorption. It can be used for housing parts, threaded bolts, and distance pieces.Information provided by CENTROPLAST Engineer..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
150
°C @Thickness 6.40 mm |
302
°F @Thickness 0.252 in |
ASTM D648 |
|
BLUESTAR LXS 315 PPE-PS
Typical Applications: Spinning industrial partsInformation provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
Asahi Kasei Thermylene® P6-40FM-2371 40% Glass Fiber/Mica Reinforced, Heat Stabilized
Information provided by Asahi Thermofil
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75-1/-2 |
|
BASF Ultramid® B3GK24 BK 00564 10/20% Glass/Glass Bead Filled PA6 (Dry)
Description: combined 10% glass-fiber and 20% glass-bead reinforced injection-molding grade for technical articles of very good dimensional stability, for instance, vehicle ash tray housings and ele..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
A. Schulman ComAlloy Hiloy® 636 Nylon 6/6, Glass/Mineral Reinforced, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
Asahi Kasei Xyron® X9108 Modified Polyphenylene Ether
High-Heat ResistantInformation provided by Asahi Kasei
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FXP 6630 Nylon 6.6 Polypropylene Alloy
DescriptionPolyfort® FXP 6630 is a nylon 6.6 / polypropylene alloy with 30% wollastonite.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | 0.5 inch; ASTM D648 |
|
PlastxWorld CEVIAN® A2604 20% GF PA/ABS Alloy, Conditioned
Property data is for samples at equilibrium moisture (1.1%)These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWo..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 - 170 °C | 302 - 338 °F | ISO 75 Af |
|
Vyncolit 3520 CG Novolac Phenolic
Graphite filled phenolic molding compound with excellent dimensional stability. Self-lubricating and has a low coefficient of friction. Not suitable for electrical applications.USES: Gas meter par..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
|
A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene
DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman.
|
|||