- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 374 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 374 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Annealed; ISO 75-2/A |
|
PolyOne Nymax™ GMF 604 40 UV Black 115 1 X 1 Polyamide 6 (Nylon 6)
The Nymax® GMF 600 Series of compounds are based upon nylon 6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part perfor..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | |
|
Plastcom SLOVAMID 66 HI/1 PA66, improved strength
FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
190
°C <br>@Thickness 3.20 mm
|
374
°F <br>@Thickness 0.126 in
|
ASTM D648 |
|
Ovation Polymers RIGITRON 20433 GF PBT, 33% Glass Reinforced
PBT - Glass reinforced (33 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared acco..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB SCANMID 6 B32^ E F30 Nylon 6, Glass Fiber Reinforced, Modified
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 - 218 °C | 374 - 425 °F | Average value: 207 °C Grade Count:62 |
|
Overview of materials for Nylon 610, Glass Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610, Glass Reinforced". Each property range of values reported is minimum and maximum values of ap..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
|
Lanxess Durethan® BKV 115 H2.0 901510 Copolyamide, 15% Glass Fiber
CoPA, injection molding grade, 15% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 15, even in..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1, -2 |
|
Lanxess Pocan® ECO T 3215 000000 PBT + PET, 15% Glass Fiber
PBT + PET, 15% glass fibers, injection molding, improved surface finish, contains 30% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics ULTEM 1000FC PEI (Europe-Africa-Middle East)
Transparent, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0, V2 and 5VA listing. US FDA and EU Food Contact compliant. NSF-51 certified for selected colors.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Ultem 1100EF PEI
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, U.S. FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
190
°C <br>@Thickness 6.40 mm
|
374
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM AUT195 PEI+PCE
High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (SABIC test method).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
190
°C <br>@Thickness 3.20 mm
|
374
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® 8032UX PBT+PET (Asia Pacific)
VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
190
°C <br>@Thickness 6.40 mm
|
374
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® DR51 PBT (Asia Pacific)
15% GR polyester, excellent mechanical, thermal and electrical performance. Non-flame retardant. Spotlights, appliance housings, handles, connectors
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
190
°C <br>@Thickness 3.20 mm
|
374
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® ENH8530 PBT+PET (Europe-Africa-Middle East)
Non-Brominated & Non-Chlorinated Flame Retardant, 15% Glass fiber reinforced PBT/PET blend
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Valox® VX8532 PBT+PET (Europe-Africa-Middle East)
VALOX VX8532 is a 30% glassfiber reinforced, non blooming, flame retardant PBT+PET blend with excellent surface appearance and good ultrasonic weldability properties.This data was supplied by SABIC-..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Valox® IQNH4550 PBT (Europe-Africa-Middle East)
Valox* iQNH4550 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 31% based on EPEAT..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75 |
|
Ter Hell Plastic Terez® PA 6 7751 TGF 15 GL Polyamide 6, 15% Glass Fiber
Description: Medium viscosity, dry impact resistant PA 6, 15% glass fiber reinforced and improved surface gloss.Application: For molding parts with good stiffness and high dimensional stability.In..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM D648 |
|
Plenco 4327 Phenolic, Granular, Compression Molded
PLENCO 04327 is a heat resistant mineral filled phenolic molding compound offering excellent cosmetic characteristics and improved heat resistant properties. PLENCO 04327 is not intended for electri..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM D648 |
|
Plenco 6343 Phenolic, Granular, Compression Molded
PLENCO 06343 is a mica reinforced phenolic molding compound, offering for a low power factor, low electrical losses, and good electrical properties after long exposures to high humidity. UL recogniz..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | DIN 53461 |
|
Polyram PlusTek PB320G3 Nylon 6, 15% Glass Fiber, Flame Retardant
15% glass-fiber reinforced, flame retardant polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
|
DSM Stanyl® TE341 Nylon 46 (European Grade) (Dry)
Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | dry; ISO 75-1/-2 |
|
DSM Stanyl® TW341-N PA46
Heat Stabilized, Lubricated
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® TSGK-30/4 X PA666-(GF+GB)30
Product description: Grilon TSGK-30 X/4 is a heat stabilized PA 66 + PA 6 injection molding grade with a 30% reinforcement combination (glass fibers and glass beads). Grilon TSGK-30/4 X has the foll..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | |
|
Aclo Accutech Nylon 6 NY0730G20L Glass Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
|
BASF Ultramid® B3EG3 15% Glass Filled PA6 (Dry)
Description: 15% glass-fiber reinforced injection-molding grade with enhanced impact resistance, for example, for vehicle mirror housings as well as for the wheels of mountain bikes.Information prov..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 179 |
|
CP-Polymer-Technik Wellamid® 6000 CF 10 HWCP 10% Carbon Fiber Nylon 6, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Valox® VX4510 PBT (Europe-Africa-Middle East)
VALOX VX4510 is a flame retarded, 10% glassfiber reinforced injection moulding PBT resin.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | DIN 53461; ASTM D648 |
|
Kolon SPELLOY® KB133G30 PC + PBT Alloy Resin
(discontinued **)
SPELLOY® is a new technology of thermoplastic Polymer alloys developed to provide unique combination of excellent mechanical properties.High impact resistance (at low temperature), good dimensional..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | DIN 53461 |
|
Qualchem Danamid FGFL0-20 Polyamide 6, 20% Glass Fiber
Reinforced with glass fiber. Flame retardant, with halogens (V-0)Information provided by Qualchem Zrt.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | DIN 53461 |
|
Polyram PlusTek PB312J6 Nylon 6, 30% Glass Fiber
30% glass-fiber reinforced polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||