- HOME
- POLYMER SEARCH
- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 387 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 387 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ISO 75-1, -2 |
|
Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber
PA 6, 30% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12
LNP* LUBRICOMP* IFL34 is a compound based on Nylon 6/12 resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 (Asia Pacific)
LNP* Lubricomp* IFL34 is a compound based on Nylon 6/12 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1010A PEI (Europe-Africa-Middle East)
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1010K PEI (Asia Pacific)
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1010KM PEI (Europe-Africa-Middle East)
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1110R PEI (Asia Pacific)
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 1110V PEI (Europe-Africa-Middle East)
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® IQ8280SF PBT+PET
Valox iQ8280SF resin is an environmentally responsible, low carbon footprint, and sustainable resin. Valox iQ8280SF resin offer Super High Flow characteristics combined with high modulus and excell..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® V4860HR PBT
30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Stat-kon PE002 PA 6 (Asia Pacific)
LNP* Stat-kon* PE002 is a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia P..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP PH0400CX PA 6
LNP* THERMOCOMP* PH0400CX is a compound based on Nylon 6 resin. Added feature of this grade is: High Specific Gravity.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP PH0400CX_BK1D466 PA 6
4.0 specific gravity, Nylon 6
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10
LNP* THERMOCOMP* QF0069 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | 80*10*4 s=60mm; ISO 75-1 a |
|
Sax Polymers SAXAMID 126F4MW4 Nylon 6, 40% Glass Fiber and Mineral Reinforced
SAXAMID 126F4MW4 is a 40% glass fibers/ mineral reinforced polyamide 6 injection-molding-grade. It has dimensional stability and high strength.Information provided by SAX Polymers
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
Annealed; ASTM D648 |
|
Solvay Specialty Polymers Acudel® 22000 Polyphenylsulfone, Modified (PPSU, Modified)
Acudel® 22000 is a modified polyphenylsulfone. It is a high-heat, high-performance resin formulation exhibiting very good hydrolytic stability, excellent resistance to acids and bases and good re..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics ULTEM HU2410 PEI (Asia Pacific)
40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Ultem HU2410 PEI (Europe-Africa-Middle East)
40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications.
Healthcare management of change, biocompatible (ISO 10993 or USP..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 6.40 mm |
387
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL GTX CRN720V PPE+PA6 (Asia Pacific)
GF20% FR-GTX, Restricted to sell for new customers
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ISO 75-1, 2 |
|
Polyplastics Duranex® 303RA Polybutylene Terephthalate (PBT), Resin adhesion improved for multiple injection molding, 30% GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ISO 75-1, 2 |
|
Polyplastics Duranex® 313RA Polybutylene Terephthalate (PBT), Resin adhesion improved for multiple injection molding, 15% GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ISO 75-1, 2 |
|
Polyplastics Duranex® 702MS Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Crastin® SK692FR BK507 Polybutylene Terephthalate (PBT)
(Unverified Data**)&l
15% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin® SK692FR is a 15% glass reinforced flame retardant polybutylene terephthalate for injection moulding.Information provided by ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
|
Eurostar Star L PA6 30V D31 PA6, Glass Filled, Injection Molding
Star L PA6 30V D31 is a Molybdenum Disulfide Lubricated, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
|
Eurostar Star L PA6 30V D51 PA6, Glass Filled, Injection Molding
Star L PA6 30V D51 is a PTFE Lubricated, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM Test |
|
BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Dry)
Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM D648 |
|
Adell BT-34 Nylon 6, 20% Glass Reinforced; Impact Modified
Data provided by Adell Plastics, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM D648 |
|
A. Schulman ComAlloy Comtuf® 615 Nylon 6, Glass Reinforced, Impact Modified
Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ASTM D648 |
|
A. Schulman ComAlloy Lubrilon® 610 Nylon 6, Carbon Fiber/PTFE Reinforced
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
197
°C @Thickness 3.20 mm |
387
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12
LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System.
|
|||