- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 42.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 42.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D495 |
|
Nylene® PX3422 Nylon 6, Impact Extrusion Grade
Dry as molded. Film Grade. Nylene PX3422 is a heat stabilized, high impact modified nylon resin designed for maximum toughness with minimum sacrifice in tensile strength and melting point. PX3422 ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75 method A |
|
Quadrant EPP Cestidur™ Polyethylene
Data provided by Quadrant Engineering Plastic Products for polymers in their European product line.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75 method A |
|
Quadrant EPP Cestlite™ ASTL Polyethylene
Data provided by Quadrant Engineering Plastic Products for polymers in their European product line.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB SCANFILL BOTTLE BY45C2 Blow Molding Grade
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75-1/-2 |
|
Quadrant EPP TIVAR® DS PE-UHMW + additives (ISO Data)
TIVAR DS is a modified PE-UHMW with extremely high molecular weight. The latter in combination with a particular manufacturing process result in a PE-UHMW grade with superior wear and abrasion resis..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75-1/-2 |
|
Quadrant EPP TIVAR® ECO PE-UHMW reprocessed (ISO Data)
This grade, partially composed of reprocessed PE-UHMW material, has an overall lower property level than the virgin TIVAR 1000 and a lower cost. Compared with virgin PE 500, however, it has a much b..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75-1/-2 |
|
Quadrant EPP TIVAR® MD PE-UHMW + metal detectable additive (ISO Data)
This PE-UHMW grade with extremely high degree of polymerisation contains a metal detectable additive which does hardly affect the inherent PE-UHMW key properties. TIVAR MD presents excellent toughne..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75-1/-2 |
|
Quadrant EPP TIVAR® SuperPlus PE-UHMW + specific additives (ISO Data)
TIVAR SuperPlus is a wear optimised, partially cross-linked PE-UHMW material with extremely high degree of polymerisation for use in most demanding applications and environments. When used for drain..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75-1/-2 |
|
Quadrant EPP TIVAR® TECH PE-UHMW + MoS2 (ISO Data)
This PE-UHMW grade with extremely high degree of polymerisation contains molybdenum disulphide, resulting in a material with improved wear resistance and sliding properties over TIVAR 1000.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75-1/-2 |
|
Polymer Industries Polyslick UHMW Rod
Polyslick UHMW Rod exhibits all of the durable qualities of our Polyslick UHMW Sheet making it perfect for the application where sheet stock is not suitable. The material is ideally suited for the m..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75-1/-2 |
|
Polymer Industries Polyslick UHMW Sheet
Polyslick UHMW Sheet exhibits the properties of excellent impact strength, abrasion resistance, low coefficient of friction, as well as very good chemical resistance. This industrial grade material ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | Compression Molded; ASTM D648 |
|
NOVA Chemicals Surpass® RMs539-U Octene sMDPE Rotational Molding Film
Features: Octene copolymerExceptional low temperature impact propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Stan..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D 648 |
|
NOVA Chemicals Novapol® TR-0535-UI Hexene MDPE Rotational Molding Resin
TR-0530-UI complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food. TR-0530-UI is su..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75 |
|
GEHR Plastics PE-UHMW Polyethylene, Ultra High Molecular Weight
The ultra high molecular weight Polyethylene has a high abrasion resistance and a high toughness at the same time. The chemical and the crack resistance are optimized in comparison to the standard P..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
42.0
°C <br>@Thickness 3.20 mm
|
108
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP FX04491H PE
LNP LUBRICOMP* FX04491H is a compound based on Polyethylene resin containing Proprietary Fillers. Added features of this material include: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
42.0
°C <br>@Thickness 3.20 mm
|
108
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP TX97446 PU
LNP* LUBRICOMP* TX97446 is a compound based on Polyurethane containing Proprietary Fillers. Added feature of this material is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D 648 |
|
Shakespeare Isocorâ„¢ SVP4011 high viscosity PA-6/69
Isocorâ„¢ 4011 is a high viscosity PA-6/69. This resin is specifically suited for applications requiring superior toughness and abrasion resistance. Isocorâ„¢ 4011 is also used in applicat..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D648 |
|
Lubrizol Stat-Rite® X-5111 Static Control Polypropylene
Stat-Rite® X-5111 is a static dissipative Polypropylene alloy. Stat-Rite® X-5111 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, permanent ES..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO-R 75 Method A |
|
Hippe PE 1000 Polyethylene
Tough, flexible and stiff, depending on the crystalline structure (density). Resinous surface. Excellent dielectric properties, Good resistance against solvents, acids and alkalis. Physiologicall..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 - 49.0 °C | 108 - 120 °F | ISO-R 75 Method A |
|
Hippe PE 300 Polyethylene
Tough, flexible and stiff, depending on the crystalline structure (density). Resinous surface. Excellent dielectric properties, Good resistance against solvents, acids and alkalis. Physiologicall..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | |
|
Arkema Group Rilsan® MA 4420 Nylon 12, Flexible Tubing Grade (Dry)
Designation ISO 1874-PA12-HI,EHL,22-003Flexible grade for tubes extrusion. Available color: black. Light and heat stabilized.Flexibility. High burst pressure and impact strength. Fit for use in a wi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D648 |
|
ExxonMobil Escorene® HD-8661 LHDPE Rotational Molding Grade
(discontinued **)
Data provided by the manufacturer, Exxon Chemical.HD-8600 series are linear high density polyethylene resins that provide outstanding environmental stress crack resistance. HD-8661 is fully formula..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D648 |
|
ExxonMobil Escorene® HD-8761 LHDPE Rotational Molding Grade
(discontinued **)
Data provided by the manufacturer, Exxon Chemical.HD-8700 series are linear high density polyethylene resins that provide outstanding environmental stress crack resistance. HD-8761 is fully formula..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75 |
|
BASF Nypel® 2351 HS BK PA6 (Dry)
Description: Nypel® 2351 HS BK is a heat stabilized, pigmented black, impact modified PA6 extrusion grade compound. Quality and performance are combines at a lower cost. It is based on recycled PA6..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75-2 |
|
CENTROPLAST CENTROLEN PE-UHMW Ultra-high molecular weight polyethylene
This plastic is a low density, easily machined material that can be welded and has a low sliding friction with high impact resistance. Applications include glide strips, pump components, and wearin..
|
|||