- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 64.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 64.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
PTS Trimid® N6-200N Nylon 6 with Nucleating Agent
Information provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75 |
|
Eastman Eastar GN002 Copolyester, Natural
(discontinued **)
Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
Eastman Eastar GN002 Copolyester, Natural
(discontinued **)
Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75 |
|
Eastman 9921P PET Injection Molded
(discontinued **)
Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | |
|
Eastman Eastapak 9921W PET
(discontinued **)
Unreinforced. ISO data as provided by the manufacturer, Eastman Chemical.This product is discontinued; 2003.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-2 |
|
Polycasa COPOL PETG
QUINN COPOL has good optical properties, brilliant surface, easy to vacuum form without pre-drying, low water absorption, very good chemical resistance, and high impact properties.Bus shelters (UV-v..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 - 248 °C | 147 - 478 °F | Average value: 99.6 °C Grade Count:41 |
|
Overview of materials for Nylon 66, MoS2 Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, MoS2 Filled". Each property range of values reported is minimum and maximum values of appropri..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | |
|
Ineos ABS TRIAX® 1220 S ABS/Nylon Blend, Dry as Molded
Extrusion and injection molding grade with good stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical dampi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12 (Asia Pacific)
LNP* Lubricomp* IL004 is a compound based on Nylon 6/12 resin containing PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP Thermocomp PB00A PA 6 (Europe-Africa-Middle East)
LNP* THERMOCOMP* PB00A is a compound based on PA 6 resin containing Glass Bead.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP WZ002 PBT
LNP* THERMOCOMP* WZ002 is a compound based on PBT resin containing 10% Milled Glass.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-LOY KX01002 Acetal Copolymer (Europe-Africa-Middle East)
LNP* Stat-Loy* KX01002 is a compound based on Acetal Copolymer resin containing Antistat. Added features include: Permanent Anti-Static.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
SK Chemicals SKYGREEN® PETG 2008 Specially Formulated PET Copolymer Resin
SKYGREEN PETG is an amorphous copolyester in which a certain amount of ethylene glycol is replaced with 1,4-cyclohexane dimethanol (CHDM), which prevent crystallization, leading to improved processa..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-2 |
|
Borealis PS65T20 Polypropylene Compound, Mineral Filled
PS65T20 is a 20% mineral filled polypropylene compound intended for injection and back injection molding. This material has excellent balanced mechanical properties and high melt flow rate. Applic..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene
DescriptionPolyfort® FPP 2661 is a injection molding grade mineral fortified impact enhanced polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene
DescriptionPolyfort® FPP 2661 is a injection molding grade mineral fortified impact enhanced polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene
DescriptionPolyfort® FPP 2661 is a injection molding grade mineral fortified impact enhanced polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-1, 2 |
|
Polyplastics Duracon® TD-30 Acetal Co-polymer (POM), High impact, Flexible
DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
Eastman Cadence™ GS2 Copolyester for film calendering
Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
Eastman Eastar DN011 Copolyester
Eastar Copolyester DN011 is a brilliantly clear polymer having excellent impact strength, chemical resistance, and low shrinkage rates. Eastar Copolyester DN011 contains a mold release.Applications/..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
Eastman Eastar DN114 Copolyester, Natural
Applications:LightingProduct Description: Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage. DN1..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
|
Eastman Eastar EN063 Polyester
Eastar Polyester EN063 is a condensation polymer produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. Eastar Polyester EN063 is a homopolymer ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
|
Eastman Tenite Butyrate 285A2R30023 Natural, Trsp Cellulose Acetate Butyrate
Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
|
Eastman Tenite Butyrate 485A2R30016 Natural Cellulose Acetate Butyrate
Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.TENITE cellulosic plastics are noted for their excellent balance of properties - toughness,..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
|
Eastman Tenite Butyrate 550E4861316 Clear, Trsp Cellulose Acetate Butyrate
Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Delrin® 100STE NC010 Acetal (POM)
(Unverified Data**)
Super Toughened High Viscosity Acetal Homopolymer with Very Low Emissions Delrin 100STE NC010 (formerly DE20590) is a high-viscosity super-toughened acetal homopolymer with very low VOC emissions. P..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-2 |
|
Denka TH-11 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene
"TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
|
Eurostar Staramide P1000IX2 PA6, Impact Modified, Injection Molded
Staramide P1000IX2 is an Impact Modified, Polyamide 6 Injection Molding Resin (also known as P1000HI010 or Star X 2010)Information provided by Eurostar.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | |
|
Arkema Group Nakan® RRS 401 L PVC, Rigid Injection Grade
NAKAN RRS 401 L is a rigid polyvinyl chloride compound developed for injection molding of waste water fittings.ISO data provided by the manufacturer, Arkema.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | |
|
3M Dyneon™ PVDF 60512/0000 Polyvinylidene Fluoride
(discontinued **)
Polyvinylidenefluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and..
|
|||