- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 82.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 82.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | annealed; ASTM D648 |
|
Plaskolite Duraplex® 100% I Impact Modified Acrylic Sheet
Continuously processed acrylic sheet.Data provided by the manufacturer, Plaskolite, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Cycolac® INP581 ABS
High flow, low molecular weight SAN.
Can be used as compounding additives for polymer blends.
Can be blended with high rubber graft modifier resins to produce customized ABS properties.
Suitable for..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 3.20 mm |
180
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycolac® MG34LG ABS
Automotive: Low gloss ABS for unpainted interior applications.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 3.20 mm |
180
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycolac® MGABS02 ABS
General purpose ABS. Excellent flow/impact.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ISO 75/Method Af |
|
Premix Thermoplastics PRE-ELEC® 12-000
PRE-ELEC 12-000 is a conductive thermoplastic compound based on a polyacetal copolymer. Conductivity is achieved by using special carbon black. In addition to a low resistivity PRE-ELEC 12-000 has a..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 3.20 mm |
180
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® FXC630SK PC+ABS (Asia Pacific)
PC+ABS, ECO-conforming flame retardant with diamond sparkle appearance.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics GELOY FXW749SK ASA
Sparkle VisualFx ASA Resin - Weatherable
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYplex PMMA 500 Acrylic Glass
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP Faradex NS0039 PC/ABS
LNP* Faradex* NS0039 is a compound based on PC/ABS resin containing Flame Retardant, Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, Flame Reta..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
|
Resirene Resirene® HF-777 General Purpose Polystyrene
Features:Medium FlowEasy ProcessingMechanical StrengthFDA Rating: 21 CFR 177.1640External Lubrication AvailableApplications:InjectionToysCassette CasesCassettesDisposablesInformation provided by US ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYabs H00 HF ABS, Heat Resistant, High Flow
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 6.35 mm |
180
°F @Thickness 0.250 in |
ASTM D-648 |
|
Chevron Phillips MC3600 Crystal Polystyrene
(discontinued **)
General purpose crystal polystyrene.Applications:HousewaresConsumer containers, vials, jars, etc.Disposable cutleryInjection molded drink cupsFeatures:Easy filling of thin-walled partsExceptional mo..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
|
Plaskolite Optix® PL-150 Acrylic Resin
(discontinued **)
Injection/extrusion pellets.Data provided by the manufacturer, Plaskolite, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 6.40 mm |
180
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP Cycoloy_C2801 PC+ABS (Europe-Africa-Middle East)
LNP* Lubricomp* Cycoloy_C2801 compound is a 5% PTFE reinforced PC+ABS wear resistant flame retardant resin for moving components in business equipment. Medium heat performance
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 6.40 mm |
180
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical HIPS 60HRI PS, Impact Modified
Description: Injection Molding, PS, General Purpose, Impact ModifiedApplication: TV Sets, Tape Recorders, Vacuum Cleaner, Washing Machine, Air ConditionerCAS: 9003-55-8Information provided by LG Che..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 6.40 mm |
180
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical HIPS MI750L PS, Impact Modified
Description: Injection Molding, PS, Impact Modified, High GlossApplication: Electric/Electronic Components, Stationary Articles, Food Containers, etc.CAS: 9003-55-8Information provided by LG Chemica..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ISO 75 |
|
GEHR Plastics POM-ELS Acetal, Electrically Conductive
Polyoxymethylene can be used in temperatures up to 100°C. The high surface strength is only surpassed by a few materials. POM shows good sliding properties and high resistance to wear and tear be..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 3.20 mm |
180
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON DD0001 PC
LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 6.40 mm |
180
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® HF-0690M ABS, Unreinforced
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 6.40 mm |
180
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® WR-9160 ASA, Unreinforced
Used in electric goods etc.Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 6.40 mm |
180
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® HG-0760AT ABS, Unreinforced
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
82.0
°C @Thickness 6.40 mm |
180
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® WR-9120AT ASA, Unreinforced
Used in washing machine cover etc.Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP WX05456 Polyester, TP
LNP THERMOCOMP* WX05456 is a compound based on Polyester, TP resin containing Mineral.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
|
Supreme Petrochem SH 731 High Impact Polystyrene
Characteristics Medium flow High Impact Excellent formability Low temperature toughnessProcessing Extrusion Molding FormingApplications Thermoformed containers, extruded profiles, packaging pro..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
|
Eastman Tenite 360A4861307 Cellulose Acetate Propionate, Clear, Trsp
Applications:Blood TherapyDrug DeliveryIV ComponentsMedical DevicesSurgical InstrumentsKey Attributes:Chemical resistance to most medical solvents including lipids and IPAEase of processingGamma and..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ISO 75-1/-2 |
|
Covestro Bayblend® FR 3000 Polycarbonate + ABS, Flame Retardant Grade
Injection molding gradeeasy-flow gradeVicat/B 120 temperature = 97 °CUL-listing 94 V-0 (1.5 mm) antimony-, chlorine- and bromine-free flame retardantglow wire test (GWFI): 960 °C (2.0 mm)no j..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ISO 75-1/-2 |
|
Covestro Makroblend® DP UT3907 Polycarbonate + PBT, Impact Grade
Developmental product(PC+PBT)-blendhigh flowimpact modifiedeasy releaseUV-stabilizedinjection molding grade Makroblend DP UT3907* offers superior flowability, good impact strength and excellent ch..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
|
Resirene Resirene® 7600 Super High Impact Polystyrene
Features:Medium FlowSuper High ImpactEasy ProcessingHigh ProductivityFDA Rating: 21 CFR 177.1640Applications:InjectionToysCompounds and Master BatchPrintersComputersRemote ControlsInformation provid..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
|
Eastman Tenite 360A4861301 Propionate Clear, Trsp
(discontinued **)
Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties if Tenite cellulosi..
|
|||
Copyright © lookpolymers.com All Rights Reserved