- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 95.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 95.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
95.0
°C @Thickness 3.20 mm |
203
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS
CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of properties
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
95.0
°C @Thickness 3.20 mm |
203
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Europe-Africa-Middle East)
CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of propertiesThis data was supplied by..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Cycoloy® CX5430 PC+ABS (Asia Pacific)
Cycoloy* resin CX5430 is a general purpose PC/ABS blend developed for thin wall applications requiring weld line strength, high flow and impact together with a good balance of other properties.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® FST3403 PC Copolymer
Lexan* FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Unannealed (0.250 in); ASTM D648 |
|
Ravago Manufacturing Americas Hysun™ 383 ASA
(discontinued **)
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Rava..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | |
|
Lehmann & Voss LUVOCOM® 80-8268 Polyacetal-copolymer, with PTFE, lubricant modified
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
95.0
°C @Thickness 6.40 mm |
203
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical LUMID GP3150A(W) PA6+MF15%, General Purpose
Feature: Injection Molding, PA6+MF15%, General PurposeApplication: E&E (Rice Cooer Housing)CAS No. 25038-54-4 and 14807-96-6Information provided by LG Chemical
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1/-2 |
|
Mitsubishi Xantar® C CM 206 Polycarbonate/ABS Blend
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
|
LG Chemical LUPOL GP-3154F General Purpose Polypropylene, 15% Mineral Fillers, High Modulus, Flame Retardant
LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | |
|
LATI Latistat 62-08 PA6
Dissipative product based on Polyamide 6 (PA6). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
95.0
°C @Thickness 3.20 mm |
203
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP KL004A Acetal Homopolymer
LNP LUBRICOMP* KL004A is a compound based on Acetal Homopolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP Lubricomp KZL34 POM
LNP* Lubricomp* KZL34 is a compound based on Acetal resin containing Milled Glass and PTFE. Characteristic of this grade is Internally Lubricated.This data was supplied by SABIC-IP for the Americas..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
95.0
°C @Thickness 3.20 mm |
203
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP RL0049S PA 66
LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Annealed; ASTM D648 |
|
Spartech Royalite R21M General Purpose ABS Resin
Data provided by the manufacturer. A general-purpose ABS resin with high impact strength, R-21M is a popular choice for a variety of products, from bicycle helmets and carrying cases to portable ta..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1/-2 |
|
Styrolution Luran® S 797 S UV White 33999 Q455 ASA
Description: Grade with especially high notched impact strengthApplications: Lighting covers and lawn mower housings.Information provided by STYROLUTION, which is a joint venture between BASF and IN..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
95.0
°C @Thickness 6.40 mm |
203
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® WR-9750H ASA, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
95.0
°C @Thickness 3.20 mm |
203
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT
LNP* LUBRICOMP* WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
|
Diamond Polymers ABS 1501
Description: Injection Molding GradeInformation provided by Diamond Polymers, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
|
E-Polymers TEKAMID® JN110 PPE+PA66 Filler Reinforced PA/PPE Alloy
Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.JN-series: PA66/PPE, PA6/P..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
|
Engineered Polymer Solutions ABS PCR 400, Recycled
General Purpose with 40% Post Consumer ABS. Natural and colors available. Injection molding grade. Uses: General PurposeInformation provided by Engineered Polymer Solutions.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75 |
|
BASF Ultraform H 2320 006 Q600 POM
Ultraform H2320 006 is a high-molecular-weight grade of POM for injection molding. It conforms to FDA requirements of 21 CFR 177.2470.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75 |
|
BASF Ultraform N 2310P Q600 POM
Ultraform N2310P Q600 is a general-purpose injection molding POM grade containing special lubricant. Low frictional coefficient giving extremely low wear with otherwise unaltered mechanical propert..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
95.0
°C @Thickness 6.40 mm |
203
°F @Thickness 0.252 in |
Method A; ASTM D648 |
|
Bhansali Engineering Abstron IM21V ABS Injection Molding Grade
Super High Gloss, High RigidityInformation provided by Bhansali
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Method A - Annealed; ASTM D-648 |
|
Bhansali Engineering Abstron IM-17A(DLW) ABS Injection Molding Grade
Medium Impact, Medium Flow ,White UndertoneInformation provided by Bhansali
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
95.0
°C @Thickness 6.40 mm |
203
°F @Thickness 0.252 in |
Method A; ASTM D648 |
|
Bhansali Engineering Santron IMS 2000 SAN Resin
Clear SANInformation provided by Bhansali
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1, 2 |
|
Polyplastics Duracon® EB-08 Acetal Co-polymer (POM), Conductive, Antistatic
DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1, 2 |
|
Polyplastics Duracon® M90-44/M90S Acetal Co-polymer (POM), Standard, General
DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
|
|||