- Polymer Property : Thermal Conductivity = 0.600 W/m-K
Polymer Property : Thermal Conductivity = 0.600 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.600 W/m-K @Temperature 80.0 °C |
4.16 BTU-in/hr-ft²-°F @Temperature 176 °F |
ASTM C518 |
| Rogers Corporation RO4533 Ceramic-Filled, Glass-Reinforced Hydrocarbon Laminate The RO4500™ Series Cost Performance Antenna Grade Laminates are ceramic-filled, glass-reinforced hydrocarbon based materials that provides the controlled dielectric constant, low loss performance a.. |
|||
| Thermal Conductivity | 0.600 W/m-K @Temperature 80.0 °C |
4.16 BTU-in/hr-ft²-°F @Temperature 176 °F |
ASTM C518 |
| Rogers Corporation RO4534 Ceramic-Filled, Glass-Reinforced Hydrocarbon Laminate The RO4500™ Series Cost Performance Antenna Grade Laminates are ceramic-filled, glass-reinforced hydrocarbon based materials that provides the controlled dielectric constant, low loss performance a.. |
|||
| Thermal Conductivity | 0.600 W/m-K @Temperature 80.0 °C |
4.16 BTU-in/hr-ft²-°F @Temperature 176 °F |
ASTM C518 |
| Rogers Corporation RT/duroid® 6002 High Frequency Laminate Features:Low loss for excellent high frequency performanceTight dielectric constant and thickness controlExcellent electrical and mechanical propertiesExtremely low thermal coefficient of dielectric.. |
|||
| Thermal Conductivity | 0.600 W/m-K @Pressure 2.07 MPa |
4.16 BTU-in/hr-ft²-°F @Pressure 300 psi |
ASTM D5470 |
| Parker Chomerics CHO-SEAL® 6330 Conductive Elastomer Description: Good performance in moderately corrosive environments; material of choice for flange finishes needing “bite-through” for good electrical contact. A low durometer hardness elastomer, i.. |
|||
| Thermal Conductivity | 0.600 - 0.800 W/m-K | 4.16 - 5.55 BTU-in/hr-ft²-°F | ASTM E1461 |
| Raschig Group 3505 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
| Thermal Conductivity | 0.600 - 0.800 W/m-K | 4.16 - 5.55 BTU-in/hr-ft²-°F | ASTM E1461 |
| Raschig Group 3535 Epoxy Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack.. |
|||
| Thermal Conductivity | 0.600 - 0.700 W/m-K | 4.16 - 4.86 BTU-in/hr-ft²-°F | ASTM E1461 |
| Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat.. |
|||
| Thermal Conductivity | 0.600 - 0.700 W/m-K | 4.16 - 4.86 BTU-in/hr-ft²-°F | ASTM E1461 |
| Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta.. |
|||
| Thermal Conductivity | 0.600 - 0.700 W/m-K | 4.16 - 4.86 BTU-in/hr-ft²-°F | ASTM E1461 |
| Raschig Group RALUPOL® 5000 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength. This product meets the all.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | ISO 8302 |
| Solvay Specialty Polymers Primef® 7010 Polyphenylene Sulfide (PPS), 65% GlassMineral
(discontinued **) Primef 7010 is a 65% mineral/glass fiber reinforced polyphenylene sulfide (PPS). This grade offers improved mechanical properties versus Primef 7002 (also 65% mineral/glass fiber), but with less flu.. |
|||
| Thermal Conductivity | 0.600 - 1.50 W/m-K | 4.16 - 10.4 BTU-in/hr-ft²-°F | Average value: 0.786 W/m-K Grade Count:7 |
| Overview of materials for Epoxy, Molded, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Mineral Filled". Each property range of values reported is minimum and maximum values of .. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | |
| Cookson Group Plaskon® PPF-165A Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A conventional molding compound specifically formulated for semiconductor devices which are molded with preplated leadframes. Lo.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | |
| Chevron Phillips Ryton® R-7 Polyphenylene Sulfide Compound
(discontinued **) Natural Color Polyphenylene Sulfide CompoundRyton® R-7 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compoun.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Lehmann & Voss LUVOCOM® 1105-8513 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Lehmann & Voss LUVOCOM® 1501/CF/30-1 Polysulfone, with carbon fiber Applications: Automotive industry, office machinery, medical- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Chemical and hydrolysis resistance parts, non.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Lehmann & Voss LUVOCOM® 20-0951 Polyphthalamide, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suita.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | HOT-DISK || 60x60x3 mm |
| Lehmann & Voss LUVOCOM® 80-7626 Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricit.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Lehmann & Voss LUVOCOM® 1105/CF/30/EM PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Lehmann & Voss LUVOCOM® 1105-7781 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Lehmann & Voss LUVOCOM® 1114-0717 PAEK, with carbon fiber and PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Good friction and wear behaviour especially at increased temperatures.Electrically conduct.. |
|||
| Thermal Conductivity | 0.600 W/m-K @Temperature 800 °C |
4.16 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Zircar Refractory Composites RS-Cloth Refractory Sheet Refractory Sheet RS-Cloth is ceramic fiber reinforced alumina composite. It offers the strength, durability, flexibility and versatility required by many high temperature applications up to 1300°C(.. |
|||
| Thermal Conductivity | 0.600 W/m-K @Temperature 800 °C |
4.16 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Zircar Refractory Composites RS-Tape Refractory Sheet Refractory Sheet RS-Tape is ceramic fiber reinforced alumina composite. It offers the strength, durability, flexibility and versatility required by many high temperature applications up to 1300°C(2.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | |
| Trelleborg Emerson & Cuming Stycast® G-508-1 One-Component Epoxy Flame Retardant Encapsulant Features and Typical ApplicationsProvide flame resistance down to 1/8 of an inch. These products also offer various other features such as thermal shock protection, low viscosity, and thermal conduc.. |
|||
| Thermal Conductivity | 0.600 W/m-K @Pressure 2.07 MPa |
4.16 BTU-in/hr-ft²-°F @Pressure 300 psi |
ASTM D5470 |
| Parker Chomerics CHO-SEAL® S6600 Conductive Elastomer Description: Low-end shielding and ESD protection; high tensile strength; no corrosion or fluid resistance.Molded onlyRoHS CompliantInformation provided by Chomerics |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52 612 |
| 3M Dyneon™ TFM™ 4220 Modified PTFE, 2% Cond. Pigm. Filled
(discontinued **) Applications include antistat linings, seals, gaskets, moldings.Data provided by Dyneon. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | |
| Trelleborg Emerson & Cuming Stycast® 2651MM/11 Two-Component General Purpose Encapsulant Features and Typical Applications: Designed as general purpose encapsulants, these products offer a wide range of features including thermal conductivity, mechanical shock and impact resistance, as .. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | |
| Chevron Phillips Ryton® R-7 02 Polyphenylene Sulfide Compound
(discontinued **) Black Polyphenylene Sulfide CompoundRyton® R-7 02 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compound wit.. |
|||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | |
| Loctite® Output™ 383 Acrylic Adhesive Acrylic Bonding Adhesives and Thermally Conductive BondersLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impa.. |
|||