- Polymer Property : Mold Temperature = 170 °C
Polymer Property : Mold Temperature = 170 °C Product List
Processing PropertiesTips: 30 items are displayed at most.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | Injection molding |
|
Hexion Bakelite™ MP 4165 Melamine Phenolic Resin, Copper Adhesive, Low Shrinkage, High Mechanical Strength
(d
Melamine/phenolic molding compound, inorganically filled, glass fiber reinforced, good temperature stability, high level of mechanical properties, copper adhesive, flammability UL 94/V-0/1.6 mm (not..
|
|||
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | Compression molding |
|
Hexion Bakelite™ MP 4165 Melamine Phenolic Resin, Copper Adhesive, Low Shrinkage, High Mechanical Strength
(d
Melamine/phenolic molding compound, inorganically filled, glass fiber reinforced, good temperature stability, high level of mechanical properties, copper adhesive, flammability UL 94/V-0/1.6 mm (not..
|
|||
| Mold Temperature | 140 - 170 °C | 284 - 338 °F | |
|
Lehmann & Voss LUVOCOM® 1500-0871 Polysulfone, with glass spheres
Applications: Isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Control disks, ca..
|
|||
| Mold Temperature | 140 - 170 °C | 284 - 338 °F | |
|
Lehmann & Voss LUVOCOM® 1500-8299 Polysulfone, with PTFE, lubricant modified
Applications: Isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Control disks, ca..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
Lehmann & Voss LUVOCOM® 1502-7866/GN4 PPSU, unreinforced
Applications: Automotive industry, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical res..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
Lehmann & Voss LUVOCOM® 1502-7867/BL4 PPSU, unreinforced
Applications: Automotive industry, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical res..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Laramid G/30-V0HF1 PPA, 30% Glass Fiber Reinforced, Flame Retardant
Semi-aromatic polyamide (PPA) based compound. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good thermal properties. Good chemical resistance. Low..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Laramid G/45 PPA, 45% Glass Fiber Reinforced
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; ..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Laramid G/50 PPA, 50% Glass Fiber Reinforced
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; ..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
Lehmann & Voss LUVOCOM® 1502-7865/BK2 PPSU, unreinforced
Applications: Automotive industry, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical res..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Laramid CE/60 PPA, 60% Mineral Reinforced
Semi-aromatic polyamide (PPA) based compound. Mineral filler. High dimensional stability. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; ..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Laramid G/15 PPA, 15% Glass Fiber Reinforced
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; ..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Laramid G/30 PPA, 30% Glass Fiber Reinforced
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; ..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Laramid G/60 PPA, 60% Glass Fiber Reinforced
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; ..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Laramid K/40 HM PPA, 40% Carbon Fiber Reinforced
Semi-aromatic polyamide (PPA) based compound. Carbon fiber. High tensile modulus. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; ..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Latigloss 57 G/40 F2 PPA, 40% Glass Fiber Reinforced
Product with high mechanical properties and exceptional surface finish based on Semi-aromatic polyamide (PPA). Glass fibers. Potentially suitable for food/medical contact applicationAvailability: Af..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Latigloss 57 G/50 F2 PPA, 50% Glass Fiber Reinforced
Product with high mechanical properties and exceptional surface finish based on Semi-aromatic polyamide (PPA). Glass fibers. Potentially suitable for food/medical contact application. Availability: ..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Latigloss 57 G/60 F2 PPA, 60% Glass Fiber Reinforced
Product with high mechanical properties and exceptional surface finish based on Semi-aromatic polyamide (PPA). Glass fibers. Potentially suitable for food/medical contact application. Availability: ..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI Latilub 57-30GRTS G/20 PPA, 20% Glass Fiber Reinforced
Self-lubricating product based on Semi-aromatic polyamide (PPA). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu..
|
|||
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | |
|
Amity Thermosets ATS 134 Phenolic Molding Inorganic, graphite Filler, Compression Molded
Characteristics: Low coefficient of frictionSelf lubricating ( graphite modified )Good thermal conductivityGood glide propertiesNot suitable for electrical applicationColor- black gray Soft/medium f..
|
|||
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | |
|
Amity Thermosets ATS 166 Phenolic Molding Chopped cotton fabric Filler, Compression Molded
Characteristics:High impact strengthGlossy surfaceLow shrinkageGood sliding propertiesColor-BlackMedium flowApplications:Cog wheelsCastor wheelsBush bearingsPulleysWelding rod handlesTextile bobbins..
|
|||
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | |
|
Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Compression Molded
Characteristics:Ammonia freeGood mouldabilityGood mechanical strengthGood electrical insulationGood surface finishMedium thermal stability Color-black, brownSoft/medium flow Applications:Telecommuni..
|
|||
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | |
|
Amity Thermosets ATS 131 Phenolic Molding Organic and graphite Filler, Compression Molded
Characteristics:Self lubricating ( graphite modified )Good glide propertiesGood sealing propertiesMedium or low mechanical strengthUnsuitable for electrical applicationGlossy surfaceThermal conducti..
|
|||
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | |
|
Amity Thermosets ATS 766 Phenolic Molding Chopped cotton fabric Filler, Compression Molded
Characteristics:High impact strengthGlossy surfaceLow shrinkageGood sliding propertiesColor-BrownMedium flowApplications:Cog wheelsCastor wheelsBush bearingsPulleysWelding rod handlesTextile bobbins..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
Resinoid 2002-2 Phenolic Molding, Fabric Reinforced
Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI LARAMID CE/60 60% Mineral Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**)
Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI LARAMID G/30 30% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**)
Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI LARAMID G/35 35% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**)
Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI LARAMID G/45 45% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**)
Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s..
|
|||
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
|
LATI LARAMID G/50 50% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**)
Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s..
|
|||