- Polymer Property : CTE, linear = 8.22 µin/in-°F
Polymer Property : CTE, linear = 8.22 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 20.0 - 900 °C |
8.22 µin/in-°F @Temperature 68.0 - 1650 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 760 °C |
8.22 µin/in-°F @Temperature 69.8 - 1400 °F |
|
| Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 26.0 - 538 °C |
8.22 µin/in-°F @Temperature 78.8 - 1000 °F |
|
| Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 26.0 - 538 °C |
8.22 µin/in-°F @Temperature 78.8 - 1000 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 26.0 - 538 °C |
8.22 µin/in-°F @Temperature 78.8 - 1000 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 600 °C |
8.22 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 500 °C |
8.22 µin/in-°F @Temperature 932 °F |
|
| Special Metals INCONEL® alloy 693 INCONEL alloy 693 is a new alloy from Special Metals which offers resistance to high temperature corrosion mechanisms not previously available from a nickel-based alloy. Of particular interest to t.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 100 °C |
8.22 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Carpenter 20-Mo6® Stainless Steel, Strip Data provided by Carpenter Technology Corporation.This is an austenitic stainless steel which is resistant to corrosion in hot chloride environments with low pH. It has good resistance to pitting, .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.22 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 15% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.22 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 45% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.22 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 45% Cold Reduction + Aged 538°C (1000°F)/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.22 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 53% Cold Reduction + Aged 538°C (1000°F)/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 21.0 - 316 °C |
8.22 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 65% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||