Arlon 0.020" (0.508 mm) Flexible Heater Silicone with Fiberglass Substrate (51576R020)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Silicone
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 0.020" (0.508 mm) Flexible Heater Silicone with Fiberglass Substrate (51576R020).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cured silicone rubber with a minimum thickness of 0.003 in. (0.08 mm)/ 0.008 in. (0.2 mm) Prime Coated 7628 Fiberglass/Uncured silicone rubber with a minimum thickness of 0.009 in. (0.2 mm); 0.003 in. (0.08 mm) polyethylene interleave; overall thickness 0.020 in ±0.0015 (0.51 mm ± 0.038). The shelf life is defined as the duration of time for which the product will meet the physical requirements outlined below. It does not guarantee the product’s usefulness in all applications. Color: Red. Weight: 735.8 g/m² ± 50.9 (21.7 oz./yd.² ± 1.5). Shelf Life: 6 months from date of manufacture at 23.8°C (75°F). Cure Time: 0.25 hours. Post Cure: 204°C (400°F), for 2 hours.Information provided by the manufacturer, Arlon Silicone Technologies Division.
Mechanical Properties Metric English Comments
Hardness, Shore A 40 - 50
40 - 50
Tensile Strength, Ultimate 5.58 - 6.82 MPa
809 - 989 psi
Elongation at Break 540 - 660 %
540 - 660 %
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 200 °C
392 °F
Mechanical per UL Card E54153
232 °C
450 °F
Minimum Service Temperature, Air -56.6 °C
-69.9 °F
UL RTI, Electrical 220 °C
428 °F
per UL Card E54153
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Strength >= 15.75 kV/mm
>= 400.0 kV/in
Processing Properties Metric English Comments
Processing Temperature 176.6 °C
349.9 °F
curing temp., at 0.345 MPa (50 psi)