BASF Capron® SEG3 H1 15% Glass-Filled Nylon 6 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® SEG3 H1 15% Glass-Filled Nylon 6 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron SEG3 H1 is a 15% glass reinforced nylon 6 injection molding compound exhibiting. It exhibits exceptional surface aesthetics at the slower fill speeds associated with the gas assist injection molding process. It maintains excellent strength, stiffness, high temperature performance and dimensional stability. Other attributes are: inherent chemical resistance, particularly to greases, oils and hydrocarbons.Capron SEG3 H1 is generally recommended for applications such as metal replacements, particularly thinwall parts requiring high flow.Data provided by Allied Signal.Processing: Max. water content 0.16%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 250-280 degC (482-536 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics critical, a mold surface temperature of 80-95 degC (176-203 degF) is required. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data MD
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 120 MPa
17400 psi
ASTM data at 5 mm/min.
Flexural Yield Strength 190 MPa
27600 psi
ASTM Data
Flexural Modulus 5.10 GPa
740 ksi
ASTM Data
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ASTM test
Deflection Temperature at 0.46 MPa (66 psi) 186 °C
367 °F
ASTM Data
Deflection Temperature at 1.8 MPa (264 psi) 214 °C
417 °F
ASTM Data
Processing Properties Metric English Comments
Drying Temperature 85.0 °C
185 °F
See Materials Notes