Covestro Bayblend® ET3036 FR PC/ABS Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® ET3036 FR PC/ABS Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Extrusion gradeAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Viscosity 410000 cP

@Shear Rate 1000 1/s,
Temperature 260 °C
410000 cP

@Shear Rate 1000 1/s,
Temperature 500 °F
melt viscosity; b.o. ISO 11443-A
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 50 %
>= 50 %
50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527-1,-2
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 180-A
40.0 kJ/m²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 180-A
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
219 °F
ISO 75-1,-2
Vicat Softening Point 120 °C

@Load 5.10 kg
248 °F

@Load 11.2 lb
50°C/h; ISO 306
122 °C

@Load 5.10 kg
252 °F

@Load 11.2 lb
120°C/h; ISO 306
Flammability, UL94 V-1

@Thickness 0.750 mm
V-1

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
ISO 294