LG Chemical Lupoy 1320C-07 Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, UV Stabilized
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupoy 1320C-07 Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: LUPOY PC 1320C-07 resin provides stability against ultraviolet radiations to solid or multi-wall sheets via the coextrusion of a 50 ? thick layerMain Characteristics: Proprietary formulation, Very low plate-out characteristics, Very high thermal stability and Very good color stabilityApplications: UV layer coating and Master batchCAS: 103598-77-2Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Melt Flow 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 68.0 MPa
9860 psi
50mm/min; ASTM D638
Elongation at Break 113 %
113 %
50mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
50mm/min; ASTM D638
Tensile Modulus 2.00 GPa
290 ksi
1mm/min; ASTM D638
Flexural Strength 68.0 MPa
9860 psi
50mm/min; ASTM D638
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 130 °C

@Thickness 4.00 mm
266 °F

@Thickness 0.157 in
Annealed; ASTM D648
133 °C

@Thickness 4.00 mm
271 °F

@Thickness 0.157 in
Unannealed; ASTM D648
Vicat Softening Point 138 °C

@Load 5.10 kg
280 °F

@Load 11.2 lb
50°C/hr; ASTM D1525
Flash Point >= 450 °C
>= 842 °F
Optical Properties Metric English Comments
Refractive Index 1.586
1.586
ASTM D542
Haze 0.70 - 1.5 %
0.70 - 1.5 %
ASTM D1003
Transmission, Visible 89 %
89 %
ASTM D1003
Descriptive Properties Value Comments
Autoignition Temperature >450°C