Palm Labs Adhesives Turbo Fuse Series 130PR PLASTIC & RUBBER (100 Viscosity) Rapid Bonding Adhesive

Category Polymer , Adhesive
Manufacturer Palm Labs Adhesives
Trade Name TURBO FUSE SERIES
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Palm Labs Adhesives Turbo Fuse Series 130PR PLASTIC & RUBBER (100 Viscosity) Rapid Bonding Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Palm Lab's Cyanoacrylate is a one component rapid bonding adhesive. TURBO FUSE SERIES 130PR PLASTIC & RUBBER’S advanced formula is designed to polymerize instantly by absorbing surface moisture. The product's performance has been tested with a variety of materials, and is recommended for a multitude of applications, especially on plastics and rubbers. The fast curing qualities make it especially desirable in high speed industrial production and is ideal for use in applications that require an easily handled medium viscosity adhesive. Because of the 100 viscosity, it works especially well in close to medium fitting applications such as unfinished metal to metal bonding, metal to rubber, and rubber to rubber.Part Numbers for this data: 04-130PR, 05-130PR, 06-130PR, 10-130PR, 15-130PR, 20-130PR, 25-130PR, 30-130PR, 35-130PRSoluble in Acetone, MEK, Amide, Methylene ChlorideInformation provided by Palm Laboratories Adhesives
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
Liquid State
Viscosity 90 - 110 cP
90 - 110 cP
Liquid State
Mechanical Properties Metric English Comments
Shear Strength 5.00 - 10.0 MPa
725 - 1450 psi
Cured; ASTM D1002/DIN 53283
6.00 - 9.03 MPa
870 - 1310 psi
Cured; ASTM D1002/DIN 53283
8.00 - 14.0 MPa
1160 - 2030 psi
Cured; ASTM D1002/DIN 53283
10.0 - 15.0 MPa
1450 - 2180 psi
Cured; ASTM D1002/DIN 53283
10.0 - 15.0 MPa
1450 - 2180 psi
Cured; ASTM D1002/DIN 53283
Thermal Properties Metric English Comments
CTE, linear 0.900 µm/m-°C
0.500 µin/in-°F
ASTM D696
Thermal Conductivity 0.100 W/m-K
0.694 BTU-in/hr-ft²-°F
ASTM C177
Maximum Service Temperature, Air 82.2 °C
180 °F
Cured State
Softening Point 71.1 - 76.7 °C
160 - 170 °F
Cured State
Minimum Service Temperature, Air -53.9 °C
-65.0 °F
Cured State
Flash Point 71.1 - 93.3 °C
160 - 200 °F
Liquid State (Tagliabue closed cup)
Electrical Properties Metric English Comments
Dielectric Strength 24.6 kV/mm
625 kV/in
ASTM D149
Processing Properties Metric English Comments
Shelf Life 12.0 Month
12.0 Month
Liquid State
Descriptive Properties Value Comments
Appearance Clear liquid
Liquid State
Clear-Hard
Cured State
Base compound (Resin) Surface Insensitive Ethyl Cyanoacrylate
Liquid State
Chemical Resistance 75% Initial Strength Retained
Gasoline at 22°C, at 1000hrs
80% Initial Strength Retained
Gasoline at 22°C, at 500hrs
85% Initial Strength Retained
Isopropanol at 22°C, at 500hrs
85% Initial Strength Retained
Isopropanol at 22°C, at 1000hrs
90% Initial Strength Retained
Motor Oil at 40°C, at 500hrs
90% Initial Strength Retained
Mineral Spirit at 22°C, at 500hrs
90% Initial Strength Retained
Motor Oil at 40°C, at 1000hrs
90% Initial Strength Retained
Mineral Spirit at 22°C, at 1000hrs
Gap Fill 0.20 mm
Cured State