Polymer Property : Tensile Strength, Ultimate = 958 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	958 MPa	139000 psi
Kennametal Stellite NucalloyÂ® 453 High-Silicon Nickel-Base Hardfacing Alloy Applications include chemical control valves, nuclear globe valves, nuclear gate valves, nuclear sliding parts, and pressure bars for plywood cutters.NucalloyÂ® alloys are unique, patented, high-s..
Tensile Strength, Ultimate	958 MPa @Temperature 538 Â°C	139000 psi @Temperature 1000 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Tensile Strength, Ultimate	958 MPa	139000 psi
Haynes UltimetÂ® alloy, aged 1000 hours at 871Â°C (1600Â°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	958 MPa @Thickness 50.8 mm, Temperature 371 Â°C	139000 psi @Thickness 2.00 in, Temperature 700 Â°F
Latrobe LescalloyÂ® 6305 VAC-ARC ; High Strength Alloy Steel LESCALLOY 6305 VAC-ARC steel is a modified 4140 steel with higher molybdenum and a vanadium addition. The alloy steel is generally used in the 160/180,000 psi tensile strength range obtained with a..