Braskem BU 004 HDPE Blow Molding Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem BU 004 HDPE Blow Molding Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.966 g/cc | 0.0349 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 36 hour @Thickness 3.00 mm, Temperature 23.0 °C |
36 hour @Thickness 0.118 in, Temperature 73.4 °F |
compression molded plaques; ASTM D1693B |
| Melt Flow | 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.38 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| High Load Melt Index | 42 g/10 min @Load 21.6 kg, Temperature 190 °C |
42 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Flexural Modulus | 1.781 GPa | 258.3 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Molecular Weight Distribution | Bimodal |
Users viewing this material also viewed the following:
- Materion BrushBronze® 95510 (AMS 4880) Continuous Cast 4.0" - 17.0"
- SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10 (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Blue 4500 Concentrate Based In Polyethylene
- Tipco Tipcolene® SEB 200 - 20% Chemically Coupled Glass Fiber Polypropylene Homopolymer with High Heat Stability
- Toyobo Diaflora® AS 1670B
- CP-Polymer-Technik Wellamid® 6600 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 66, Heat Stabilized, Dry
- CMW® D154X Post-Oxidized Silver Cadmium Oxide Contact Material ASTM B781 Table 3
- Latrobe Lescalloy® UT-18 VAC-ARC ; 1.75 in. round High Strength Alloy Steel
Copyright © lookpolymers.com All Rights Reserved