CRP Technology Windform® XT Polyamide-Carbon Composite

Category Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer CRP Technology
Trade Name Windform®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CRP Technology Windform® XT Polyamide-Carbon Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
WindForm™ XT Composite is a new generation material, in which the mechanical characteristics are excellent for Rapid Manufacturing. Black coloured compound polyamide and carbon based material with brilliant reflexes, WindForm™ XT is characterized by stiffness and extremely high UTS, excellent surface finish, resistance to extreme wear and an optimal reproduction of detail.Class of material: Composite polyamide based powderTechnology: Selective Laser SinteringWindForm™ XT offers an alluring, black, sparkling look, appreciable in many design applications. WindForm™ XT is particularly suited to applications which require superior mechanical properties, extremely high performance, in rapid timing. Superior price.Areas of application: aerodynamic applications in the wind tunnel, on the race track and on the road, functional prototypes for case/carter, frames, definitive windscreens for motorcycle racing and on road.Information provided by CRP Technology.
Physical Properties Metric English Comments
Density 1.101 g/cc
0.03978 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength at Break 77.85 MPa
11290 psi
UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97)
Elongation at Break 2.6 %
2.6 %
UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97)
Tensile Modulus 7.3208 GPa
1061.8 ksi
UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97)
Flexural Strength 131.52 MPa
19075 psi
UNI EN ISO 14125: 2000
Flexural Modulus 6.2485 GPa
906.28 ksi
UNI EN ISO 14125: 2000
Charpy Impact Unnotched 3.24 J/cm²
15.4 ft-lb/in²
ASTM D256 and UNI EN ISO 179:1998
Charpy Impact, Notched 0.473 J/cm²
2.25 ft-lb/in²
ASTM D256 and UNI EN ISO 179:1998
0.466 J/cm²

@Temperature -30.0 °C
2.22 ft-lb/in²

@Temperature -22.0 °F
ASTM D256 and UNI EN ISO 179:1998
Thermal Properties Metric English Comments
CTE, linear 22.7 µm/m-°C

@Temperature 46.0 °C
12.6 µin/in-°F

@Temperature 115 °F
X direction
24.6 µm/m-°C

@Temperature 80.0 °C
13.7 µin/in-°F

@Temperature 176 °F
X direction
25.7 µm/m-°C

@Temperature 46.0 - 120 °C
14.3 µin/in-°F

@Temperature 115 - 248 °F
X direction
29.8 µm/m-°C

@Temperature 120 °C
16.6 µin/in-°F

@Temperature 248 °F
X direction
90.4 µm/m-°C

@Temperature 46.0 °C
50.2 µin/in-°F

@Temperature 115 °F
Y direction
99.3 µm/m-°C

@Temperature 80.0 °C
55.2 µin/in-°F

@Temperature 176 °F
Y direction
104.8 µm/m-°C

@Temperature 46.0 - 120 °C
58.22 µin/in-°F

@Temperature 115 - 248 °F
Y direction
124.7 µm/m-°C

@Temperature 120 °C
69.28 µin/in-°F

@Temperature 248 °F
Y direction
131.8 µm/m-°C

@Temperature 46.0 °C
73.22 µin/in-°F

@Temperature 115 °F
Z direction
216.7 µm/m-°C

@Temperature 46.0 - 120 °C
120.4 µin/in-°F

@Temperature 115 - 248 °F
Z direction
230.7 µm/m-°C

@Temperature 80.0 °C
128.2 µin/in-°F

@Temperature 176 °F
Z direction
287.6 µm/m-°C

@Temperature 120 °C
159.8 µin/in-°F

@Temperature 248 °F
Z direction
Thermal Conductivity 2.119 W/m-K
14.71 BTU-in/hr-ft²-°F
Melting Point 179.3 °C
354.7 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 175.4 °C
347.7 °F
ASTM D648
Vicat Softening Point 178.1 °C
352.6 °F
10 N; ASTM D1252
Electrical Properties Metric English Comments
Electrical Resistivity 130 ohm-cm
130 ohm-cm
Descriptive Properties Value Comments
Color Black
Surface Finish 1.8 Ra µm
After Finishing
6.0 Ra µm
After SLS Process