Chosun Refractories CTC-60TD Monolithic Refractories for Ladle and Tundish
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories CTC-60TD Monolithic Refractories for Ladle and Tundish.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.002943 GPa @Temperature 110 °C, Time 86400 sec |
0.4269 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.008829 GPa @Temperature 1500 °C, Time 10800 sec |
1.281 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 19.6 MPa @Temperature 110 °C, Time 86400 sec |
2840 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 39.2 MPa @Temperature 1500 °C, Time 10800 sec |
5690 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage | 0.00 % @Temperature 110 °C, Time 86400 sec |
0.00 % @Temperature 230 °F, Time 24.0 hour |
|
| 1.75 % @Temperature 1500 °C, Time 10800 sec |
1.75 % @Temperature 2730 °F, Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 61 % | 61 % | |
| SiO2 | 34 % | 34 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Vibrating | |
| Main Applications | Tundish | |
| Material Required for Estimating (kg/?) | 2,500 | |
| Water Required for Casting(%) | 7.1 |
Users viewing this material also viewed the following:
- Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; HT (TH04) Temper; up to 9.5 mm Thickness (UNS C17000)
- Taiwan Sheen Soon Sheenthane® A8510H TPU for Ink
- SABIC Innovative Plastics LNP Thermocomp DF002L PC
- Plenco 6401 Phenolic, Briquette, Injection Molded
- DSM Arnitel® PL650 Injection Grade Copolyester Elastomer (North America)
- Clariant ABS4500 ABS, High Impact
- EMS-Grivory Grivory® BRZ 234/1 W PA6
- Ashley Polymers Ashlene® L930 Nylon 12
- Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)
- Styron Magnum™ AG700 ABS, Low Gloss
Copyright © lookpolymers.com All Rights Reserved