Dow FINGERPRINT™ DFDA-7510 NT Linear Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name FINGERPRINT™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow FINGERPRINT™ DFDA-7510 NT Linear Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FINGERPRINT™ DFDA-7510 NT resin is produced using UNIPOL™ process technology. It is intended for use in micro irrigation tube, durable hose and tube, profile extrusion, and injection molded fitting applications. Information provided by Dow
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
natural resin; ASTM D792
Environmental Stress Crack Resistance >= 500 hour
>= 500 hour
F<sub>o</sub>; Compression molded parts prepared according to ASTM D 1928, condition A.; ASTM D1693
High Load Melt Index 44 g/10 min

@Load 21.6 kg,
Temperature 190 °C
44 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Melt Index of Compound 0.60 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.60 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 44
44
Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D2240
Tensile Strength at Break 15.5 MPa
2250 psi
Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
Tensile Strength, Yield 11.0 MPa
1600 psi
Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
Elongation at Break 800 %
800 %
Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
Flexural Modulus 0.310 GPa
45.0 ksi
Compression molded parts prepared according to ASTM D 1928, method 1, procedure B.; ASTM D790
Thermal Properties Metric English Comments
Brittleness Temperature <= -100 °C
<= -148 °F
Compression molded parts prepared according to ASTM D 1928, procedure A.; ASTM D746