ExxonMobil LD 123.LN General Purpose Clarity Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Exxon Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 123.LN General Purpose Clarity Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Product Description: LD 123.LN blown film grade offers an excellent balance of optical and strength properties for general purpose clear film applications.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: YesApplications: Bread BagsCo-Extrusion FilmsCollation ShrinkDiaper BacksheetFoamsHigh Performance Collation ShrinkHygiene PackagingLabel FilmLamination FilmOverwrap FilmPaper Overwrap Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	ExxonMobil Method
Thickness	38.1 microns	1.50 mil
Melt Flow	2.4 g/10 min @Load 2.16 kg, Temperature 190 °C	2.4 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.0 MPa	1600 psi	ASTM D882
Film Tensile Strength at Yield, TD	11.7 MPa	1700 psi	ASTM D882
Film Elongation at Break, MD	270 %	270 %	ASTM D882
Film Elongation at Break, TD	660 %	660 %	ASTM D882
Puncture Energy	2.03 J	1.50 ft-lb	ExxonMobil Method
Elmendorf Tear Strength MD	480 g	480 g	ASTM D1922
Elmendorf Tear Strength TD	120 g	120 g	ASTM D1922
Dart Drop Test	100 g	0.221 lb	ASTM D1709
Film Tensile Strength at Break, MD	28.6 MPa	4150 psi	ASTM D882
Film Tensile Strength at Break, TD	24.0 MPa	3480 psi	ASTM D882
1% Secant Modulus, MD	220 MPa	31900 psi	ASTM D882
1% Secant Modulus, TD	269 MPa	39000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	112 °C	233 °F	Peak Melting Temperature; ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	5.3 %	5.3 %	ASTM D1003
Gloss	72 %	72 %	45°; ASTM D2457
Transmission, Visible	90 %	90 %	clear; thickness not quantified