Hexcel® HexPly® F650 Bismaleimide Resin with Graphite F3T584 fabric reinforcement
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F650 Bismaleimide Resin with Graphite F3T584 fabric reinforcement.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aging Data, (T300-3K, 8 H.S.); Laminate Physicals: 59.6% Fiber volume, 34.0% Resin content, 1.0% VoidsInformation provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 655 MPa @Temperature 232 °C |
95000 psi @Temperature 450 °F |
Control (Prepreg with no freezer or out time exposure) |
| 710 MPa @Temperature 232 °C |
103000 psi @Temperature 450 °F |
Phase V (Prepreg stored in freezer 1 year at -9°C and exposed to 60 days at RT) | |
| 731 MPa @Temperature 232 °C |
106000 psi @Temperature 450 °F |
Phase I (Prepreg stored in freezer 4 months at -9°C and exposed to 30 days at RT) | |
| 758 MPa @Temperature 232 °C |
110000 psi @Temperature 450 °F |
Phase II (Prepreg stored in freezer 4 months at -9°C and exposed to 60 days at RT) | |
| 814 MPa @Temperature 232 °C |
118000 psi @Temperature 450 °F |
Phase III (Prepreg stored in freezer 6 months at -9°C and exposed to 60 days at RT) | |
| 827 MPa @Temperature 232 °C |
120000 psi @Temperature 450 °F |
Phase IV (Prepreg stored in freezer 1 year at -9°C and exposed to 30 days at RT) | |
| 862 MPa @Temperature 23.0 °C |
125000 psi @Temperature 73.4 °F |
||
| 869 MPa @Temperature 23.0 °C |
126000 psi @Temperature 73.4 °F |
||
| 876 MPa @Temperature 23.0 °C |
127000 psi @Temperature 73.4 °F |
||
| 889 MPa @Temperature 23.0 °C |
129000 psi @Temperature 73.4 °F |
||
| 903 MPa @Temperature 23.0 °C |
131000 psi @Temperature 73.4 °F |
||
| 924 MPa @Temperature 23.0 °C |
134000 psi @Temperature 73.4 °F |
||
| Compressive Yield Strength | 469 MPa @Temperature 232 °C |
68000 psi @Temperature 450 °F |
Phase II (Prepreg stored in freezer 4 months at -9°C and exposed to 60 days at RT) |
| 474 MPa @Temperature 232 °C |
68700 psi @Temperature 450 °F |
Phase V (Prepreg stored in freezer 1 year at -9°C and exposed to 60 days at RT) | |
| 481 MPa @Temperature 232 °C |
69800 psi @Temperature 450 °F |
Phase III (Prepreg stored in freezer 6 months at -9°C and exposed to 60 days at RT) | |
| 499 MPa @Temperature 232 °C |
72400 psi @Temperature 450 °F |
Phase IV (Prepreg stored in freezer 1 year at -9°C and exposed to 30 days at RT) | |
| 532 MPa @Temperature 232 °C |
77200 psi @Temperature 450 °F |
Phase I (Prepreg stored in freezer 4 months at -9°C and exposed to 30 days at RT) | |
| 558 MPa @Temperature 232 °C |
80900 psi @Temperature 450 °F |
Control (Prepreg with no freezer or out time exposure) | |
| 606 MPa @Temperature 23.0 °C |
87900 psi @Temperature 73.4 °F |
||
| 623 MPa @Temperature 23.0 °C |
90400 psi @Temperature 73.4 °F |
||
| 703 MPa @Temperature 23.0 °C |
102000 psi @Temperature 73.4 °F |
||
| 710 MPa @Temperature 23.0 °C |
103000 psi @Temperature 73.4 °F |
||
| 731 MPa @Temperature 23.0 °C |
106000 psi @Temperature 73.4 °F |
||
| 738 MPa @Temperature 23.0 °C |
107000 psi @Temperature 73.4 °F |
||
| Shear Strength | 44.3 MPa @Temperature 232 °C |
6430 psi @Temperature 450 °F |
Short Beam; Phase II (Prepreg stored in freezer 4 months at -9°C and exposed to 60 days at RT) |
| 45.9 MPa @Temperature 232 °C |
6660 psi @Temperature 450 °F |
Short Beam; Phase IV (Prepreg stored in freezer 1 year at -9°C and exposed to 30 days at RT) | |
| 46.1 MPa @Temperature 232 °C |
6690 psi @Temperature 450 °F |
Short Beam; Phase I (Prepreg stored in freezer 4 months at -9°C and exposed to 30 days at RT) | |
| 47.2 MPa @Temperature 232 °C |
6850 psi @Temperature 450 °F |
Short Beam; Phase V (Prepreg stored in freezer 1 year at -9°C and exposed to 60 days at RT) | |
| 49.6 MPa @Temperature 23.0 °C |
7190 psi @Temperature 73.4 °F |
||
| 51.1 MPa @Temperature 232 °C |
7410 psi @Temperature 450 °F |
Short Beam; Phase III (Prepreg stored in freezer 6 months at -9°C and exposed to 60 days at RT) | |
| 51.7 MPa @Temperature 232 °C |
7500 psi @Temperature 450 °F |
Short Beam; Control (Prepreg with no freezer or out time exposure) | |
| 55.2 MPa @Temperature 23.0 °C |
8010 psi @Temperature 73.4 °F |
||
| 56.5 MPa @Temperature 23.0 °C |
8190 psi @Temperature 73.4 °F |
||
| 60.7 MPa @Temperature 23.0 °C |
8800 psi @Temperature 73.4 °F |
||
| 64.1 MPa @Temperature 23.0 °C |
9300 psi @Temperature 73.4 °F |
||
| 68.7 MPa @Temperature 23.0 °C |
9960 psi @Temperature 73.4 °F |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 TF-GV 1530 Nylon 6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced
- PolyOne Geon™ Vinyl Flexible R275AE White 685 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Wanhua Chemical Wanthane® WHT-8280H Super Hard Polyether-Based TPU
- DSM Stanyl® TW341 Nylon 46 (European and Asian Grade) (Dry)
- Arkema Group Nakan® FSS 703 R PVC, Soft Injection Molding Grade
- 3M FM123 Indoor UL Recognized White Polyester Label Products
- Bhansali Engineering Abstron IPM3000 PMMA- ABS Alloy
- Momentive Performance Materials PolarTherm® PT140 Boron Nitride (BN) Powder
- Teknor Apex APEX® 3065-H Polyvinyl Chloride, Flexible
- Polyplastics Duracon® CP-15X Acetal Co-polymer (POM), Creep resistant, Creep resistant
Copyright © lookpolymers.com All Rights Reserved