Hexcel® HexWeb® HRH-10 - 1/8- 5.0 Aramid Fiber/Phenolic Resin Honeycomb

Category Other Engineering Material , Composite Core Material , Polymer , Thermoset , Aramid , Phenolic
Manufacturer Hexcel
Trade Name HexWeb®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® HRH-10 - 1/8- 5.0 Aramid Fiber/Phenolic Resin Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the hexagonal or OX-Core confiation, the block is dipped in phenolic resin. After curing the resin, slices are cut to the desired thickness. For special applications, such as air directionalizing, HexWeb HRH-10 can be provided without the phenolic resin. Using this process, a wide range of cell sizes, paper thicknesses, and densities can be produced.Information provided by HexCel
Physical Properties Metric English Comments
Density 0.0801 g/cc
0.00289 lb/in³
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 3.86 MPa
>= 560 psi
Bare, min
>= 4.27 MPa
>= 620 psi
Stabilized, min
4.83 MPa
700 psi
Bare, typ
5.31 MPa
770 psi
Stabilized, typ
Compressive Modulus 0.255 GPa
37.0 ksi
Stabilized, typ
Shear Modulus 0.0372 GPa
5.40 ksi
Plate Shear, W Direction, typ
0.0703 GPa
10.2 ksi
Plate Shear, L Direction, typ
Shear Strength >= 1.03 MPa
>= 150 psi
Plate Shear, W Direction, min
1.21 MPa
175 psi
Plate Shear, W Direction, typ
>= 1.90 MPa
>= 275 psi
Plate Shear, L Direction, min
2.24 MPa
325 psi
Plate Shear, L Direction, typ