- Honeywell ACLAR® SupRx 900 CTFE Homopolymer, Barrier Film
Honeywell ACLAR® SupRx 900 CTFE Homopolymer, Barrier Film
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | Honeywell |
| Trade Name | ACLAR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell ACLAR® SupRx 900 CTFE Homopolymer, Barrier Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ACLAR® SupRx 900 is a .9 mil CTFE homopolymer high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.11 g/cc | 2.11 g/cc | ASTM D1505 |
| Density | 2.10 g/cc | 0.0760 lb/in³ | Yield Density |
| Water Vapor Transmission | 0.0280 g/m²/day | 0.00180 g/100 in²/day | 77°F (25°C) / 60%RH; ASTM F1249 |
| 0.0470 g/m²/day | 0.00303 g/100 in²/day | 86°F (30°C) / 60%RH; ASTM F1249 | |
| 0.0590 g/m²/day | 0.00380 g/100 in²/day | 86°F (30°C) / 65% RH; ASTM F1249 | |
| 0.202 g/m²/day | 0.0130 g/100 in²/day | 104°F (40°C) / 75%RH; ASTM F1249 | |
| 0.264 g/m²/day | 0.0170 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 | |
| Thickness | 22.9 microns | 0.900 mil | |
| Surface Tension | >= 42 dynes/cm | >= 42 dynes/cm | treated side; ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 100 - 150 % | 100 - 150 % | ASTM D882 |
| Film Elongation at Break, TD | 200 - 275 % | 200 - 275 % | ASTM D882 |
| Secant Modulus, MD | 1.310 - 1.551 GPa | 190.0 - 225.0 ksi | ASTM D882 |
| Secant Modulus, TD | 1.138 - 1.448 GPa | 165.1 - 210.0 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 75.8 - 110 MPa | 11000 - 16000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 41.4 - 49.6 MPa | 6000 - 7200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 211 °C | 412 °F | crystalline melting point; ASTM D4591 |
| Shrinkage, MD | <= 12 % | <= 12 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | <= -12.0 % | <= -12.0 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Quadrant EPP Proteus® HDPE - High Density Polyethylene (ASTM Product Data Sheet)
- LATI Latiohm 66-05 PD01 G/20 PA66, 20% Glass Fiber Reinforced
- Teknor Apex Monprene® MP-1563 Thermoplastic Elastomer
- SABIC Innovative Plastics NORYL PCN2615H PPE+PS (Asia Pacific)
- EMS-Grivory Grivory® BG-25 S PA6-GF25
- EMS-Grivory Grivory® TSM-40/4 PA666-MD40
- Arkema Group Pebax® MX 1059 Polyether Block Amide (PEBA) (Conditioned)
- BASF Ultramid® A3WG6 30% Glass Filled PA66 (Dry)
- 3M Scotchcal™ 3632-22 Translucent Film
- DuPont Teijin Films Mylar® M30 Polyester Film, 50 Gauge (14 µm), PVDC Coated (discontinued **)
Copyright © lookpolymers.com All Rights Reserved