Iran Petrochemical (PCC) MF3713 High Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Extruded , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | Iran Petrochemical Commercial Co. (PCC) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Iran Petrochemical (PCC) MF3713 High Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MF3713 is a high molecular weight high density polyethylene.Applications: bags, products for use in property modification.Information provided by Iran Petrochemical Commercial Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ISO 1183 |
| Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| 13 g/10 min @Load 21.6 kg, Temperature 190 °C |
13 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 550 % | 550 % | ISO 527-1 |
| Film Elongation at Break, TD | 650 % | 650 % | ISO 527-1 |
| Tensile Modulus | 0.735 GPa | 107 ksi | ISO 527-1 |
| Elmendorf Tear Strength MD | 21.4 g | 21.4 g | ISO 6383-2 |
| Elmendorf Tear Strength TD | 112 g | 112 g | ISO 6383-2 |
| Film Tensile Strength at Break, MD | <= 46.0 MPa | <= 6670 psi | ISO 527-1.3 |
| Film Tensile Strength at Break, TD | <= 46.0 MPa | <= 6670 psi | ISO 527-1.3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 121 °C | 250 °F | ISO 306 |
Users viewing this material also viewed the following:
- NanoAmor 20% DWNT Double Walled Carbon Nanotubes
- Nilit Nilamon A3 H K8 40% Mineral Reinforced PA66
- SABIC Innovative Plastics Lexan® HP4REU PC (Europe-Africa-Middle East)
- Lubriplate SYN LUBE 68 PAO-Based Multi-Purpose Synthetic Fluid
- Karina 828-08/20-AY-ERYB-PO Beige PVC Compound
- Special Metals NILO® Alloy 36 Low-Expansion Alloy
- A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 60A, Non-Black Peroxide Cure
- DSM Stanyl® TW200F3 (COND) Nylon 46 15% Glass Reinforced, Heat Stabilized (North America)
- Solvay Specialty Polymers Diofan® A 736 Polyvinylidene Chloride (PVDC)
Copyright © lookpolymers.com All Rights Reserved