LG Chemical HYPERIER IP1306B PA-HDPE Nanoclay Compound
| Category | Polymer , Thermoplastic , Nylon , Polyethylene (PE) , HDPE |
| Manufacturer | LG Chemical |
| Trade Name | HYPERIER |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical HYPERIER IP1306B PA-HDPE Nanoclay Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
HYPERIER is a nano compound made from nano-sized inorganic plate clay. Blow Molding, Barrier thermoplastic, Nylon blend with HDPEApplication: Agrochemical Container, SORE* Fuel Tank, PFCCAS No. 9002-88-4 and 25038- 54- 4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Blow Molding |
| Melt Flow | 0.35 - 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.35 - 0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.05 MPa @Thickness 3.20 mm |
3633 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 262.7 % @Thickness 3.20 mm |
262.7 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 31.5 MPa @Thickness 6.40 mm |
4570 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 0.8360 GPa @Thickness 6.40 mm |
121.3 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.667 J/cm @Thickness 6.40 mm, Temperature -40.0 °C |
1.25 ft-lb/in @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| 6.41 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
12.0 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 175 - 215 °C | 347 - 419 °F | Blow Molding |
| Middle Barrel Temperature | 175 - 215 °C | 347 - 419 °F | Blow Molding |
| Front Barrel Temperature | 175 - 215 °C | 347 - 419 °F | Blow Molding |
| Die Temperature | 175 - 215 °C | 347 - 419 °F | Blow Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Blow Molding |
| Head Temperature | 175 - 215 °C | 347 - 419 °F | Blow Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Blow Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Blow Molding |
| Screw Speed | 10 - 50 rpm | 10 - 50 rpm | Blow Molding |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3653T TPE, PP Overmold or Standalone use
- Polymax® Maxelast® P3990H TPE, PP Overmold or Standalone use
- PTS Trimid® N66-100HL Heat Stabilized, Lubed Nylon 6/6
- Indium Corp. #2212-10 Wave Solder Flux
- LG Chemical HIPS MI730 PS, Impact Modified
- SABIC Innovative Plastics NORYL PX6120 PPE+PS (Asia Pacific)
- Teknor Apex Monprene® MP-2156 Thermoplastic Elastomer
- Polyplastics Duracon® SX-35 Acetal Co-polymer (POM), Flexible, Lower noise
- Arlon R29609R020 Silicone Rubber with Fiberglass Substrate
- Beijing Evergrow Resources PTFE Bar
Copyright © lookpolymers.com All Rights Reserved