M. Holland Company LL106 LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Sheeting Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF M. Holland Company LL106 LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Additives: Antiblock, SlipFeatures: Unspecified Antiblocking, Hexane Comonomer, Copolymer, Good Drawdown, Good Processability, Unspecified SlipUses: Film, LinersApprovals: FDA 21 CFR 177.1520(c) 2.2 and FDA 21 CFR 176.170, Table 2, Cond. B, D, E, F, G and HProcessing Method: Blown FilmInformation provided by M. Holland.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 31.8 microns
1.25 mil
Melt Flow 0.90 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.90 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 440 %
440 %
ASTM D882
Film Elongation at Break, TD 580 %
580 %
ASTM D882
Secant Modulus, MD 0.255 GPa
37.0 ksi
1% Strain; ASTM D882
Secant Modulus, TD 0.317 GPa
46.0 ksi
1% Strain; ASTM D882
Coefficient of Friction 0.13
0.13
ASTM D1894
Elmendorf Tear Strength MD 400 g
400 g
ASTM D1922
Elmendorf Tear Strength TD 910 g
910 g
ASTM D1922
Dart Drop Test 130 g
0.287 lb
ASTM D1709
Film Tensile Strength at Break, MD 29.6 MPa
4300 psi
ASTM D882
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ASTM D882
Processing Properties Metric English Comments
Melt Temperature 182 - 221 °C
360 - 430 °F
Blow-up Ratio (BUR) 1.5 - 2.5
1.5 - 2.5