- M. Holland Company MAGMA® LM311-DX LLDPE (discontinued **)
M. Holland Company MAGMA® LM311-DX LLDPE (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | M. Holland Company MAGMA® LM311-DX LLDPE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Good Processability, Good Puncture Resistance, Good Tear Strength, Good ToughnessProcessing Method: ExtrusionInformation provided by M. Holland.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.875 g/cc | 0.0316 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 4.5 g/10 min | 4.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 950 % | 950 % | ASTM D882 |
| Film Elongation at Break, TD | 980 % | 980 % | ASTM D882 |
| Elmendorf Tear Strength MD | 580 g | 580 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 820 g | 820 g | ASTM D1922 |
| Dart Drop Test | >= 1000 g | >= 2.20 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 56.5 MPa | 8200 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 47.0 MPa | 6820 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 75.0 °C | 167 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | <= 154 °C | <= 310 °F | |
| Zone 1 | 154 °C | 310 °F | |
| Melt Temperature | 166 - 204 °C | 330 - 400 °F | |
| Die Opening | 0.0810 - 0.254 cm | 0.0319 - 0.100 in | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets |
Users viewing this material also viewed the following:
- Performance Polymers IPS II PPL-A1050 PEKK (Polyetherketoneketone) Branched Standard Grade
- Aardvark Polymers AARTEL® 2000 Rotational Molding Resin
- LG Chemical Methyl Acrylate
- SABIC Innovative Plastics LNP THERMOCOMP 9X04488 POLYPHENYLENESULFONE (Asia Pacific)
- A. Schulman POLYFORT™ PP 7001
- A. Schulman FORMION™ FI 231 5% Mineral Reinforced Ionomer / Nylon Alloy
- Borealis Borstar® MB7542 High Density Polyethylene for Injection Molding
- Eastman Tritan FX100 Copolyester
- Vyncolit X611 Novolac Phenolic
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR Sulfur
Copyright © lookpolymers.com All Rights Reserved