Multibase Multi-Pro® 2520 XU Black Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 2520 XU Black Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0081 cm/cm | 0.0081 in/in | ASTM D955 |
| Melt Flow | 5.25 g/10 min | 5.25 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 16.8 MPa | 2440 psi | ASTM D638 |
| Elongation at Break | 140 % | 140 % | ASTM D638 |
| Flexural Strength | 16.9 MPa | 2450 psi | ASTM D790 |
| Flexural Modulus | 1.28 GPa | 186 ksi | 1% Secant; ASTM D790 |
| Izod Impact, Notched | 1.76 J/cm | 3.29 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 16.83 J | 12.42 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.9 °C | 201 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.1 °C | 133 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66/6 HI/1 PA66/6, improved strength
- Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F)
- LATI Latene® 22H2 MX/25 PP Homopolymer, Heat Stabilized
- Spartech Royalite R6000 FR-PC Aircraft Grade Sheet
- Samsung Cheil Industries Infino® XP-2140C PPS
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- Tisan TISLAMID® 6 30% Glass Filled Impact Modified, Heat Stabilized Nylon 6
- Wellman Wellamid® MR410 22H-WBK 40% Mineral Reinforced, Weatherable Black Nylon 66
- Total PPR 7220 Random Copolymer Polypropylene, Injection Molding
- ExxonMobil LLDPE LL 8450.31 Linear Low Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved