NIZHNEKAMSKNEFTEKHIM PE 6152C (526H3) High Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | NIZHNEKAMSKNEFTEKHIM Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NIZHNEKAMSKNEFTEKHIM PE 6152C (526H3) High Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 - 0.954 g/cc | 0.0343 - 0.0345 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 0.25 - 0.40 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.25 - 0.40 g/10 min @Load 11.0 lb, Temperature 374 °F |
ASTM D1283/L |
| 5.0 - 8.0 g/10 min @Load 21.6 kg, Temperature 190 °C |
5.0 - 8.0 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@5kg ratio > 20; ASTM D1283 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 55.0 MPa | >= 7980 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | >= 48.0 MPa | >= 6960 psi | ASTM D882 |
| Film Elongation at Break, MD | >= 450 % | >= 450 % | ASTM D882 |
| Film Elongation at Break, TD | >= 550 % | >= 550 % | ASTM D882 |
| Tensile Modulus | >= 0.800 GPa | >= 116 ksi | 2% sec, TD; ASTM D882 |
| >= 0.900 GPa | >= 131 ksi | 2% sec, MD; ASTM D882 | |
| Elmendorf Tear Strength, MD | >= 0.512 g/micron | >= 13.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | >= 2.36 g/micron | >= 60.0 g/mil | ASTM D1922 |
| Dart Drop Test | >= 150 g | >= 0.331 lb | ASTM D1709 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel Content (pcs./m²) | 600 |
Users viewing this material also viewed the following:
- PolyOne Bergadur™ PB40 G30 UF UV Polybutylene Terephthalate (PBT)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N990 Filler
- DuPont Performance Polymers Zytel® 70G30L NC010 Nylon 66 (Unverified Data**)
- KB Alloys 20% Iron Aluminum Alloy
- Solvay Sulfuric Acid 93% Paper Grade
- Plenco 5118 Phenolic, Granular, Injection Molded
- Epoxy Technology EPO-TEK® 360 Low Viscosity Optical Epoxy Adhesive
- Johnson Matthey Matti-sil 38Sn Cadmium Free Brazing Alloy
Copyright © lookpolymers.com All Rights Reserved